LNP™ KONDUIT™ Compound 8TF29E

LNP KONDUIT 8TF29E compound is based on Liquid Crystal Polymer (LCP) resin containing 10% glass fibers proprietary thermal filler. Added features of this grade include: Thermally Conductive, Electrically Insulative, High flow, Low Moisture absorption, Low CTE values. This product is available in dark colours only.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Liquid Crystal Polymer (LCP)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

High Flow
High temperature resistance
Low Moisture Absorption
No PFAS intentionally added
Thermally conductive/Electrically isolative

Industry

Material previously used in

Electronic Components
Material Handling

Applications

Possible usage of material

Fog Lamp
Industrial Material Handling
Semiconductor
led
electronic component
burn-in test socket
bits
test socket
carrier tape
foup
thermal conductive
lens folder
flash light
camera
wireless
heat sink
thermal management
thermal dissipation
thermistor
cooling fin
electronics housing
electric vehicle
wafer basket
ic chip carrier
low extraction
wafer handling
hard drive

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+14	Ω	ASTM D257
Volume Resistivity	1.E+15	Ω.cm	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	47	J/m	ASTM D256
Izod Impact, notched, -30°C	40	J/m	ASTM D256
Izod Impact, unnotched, 23°C	200	J/m	ASTM D4812
Izod Impact, unnotched, -30°C	230	J/m	ASTM D4812
*Izod Impact, notched 80103 +23°C*	5.2	kJ/m²	ISO 180/1A
*Izod Impact, notched 80103 -30°C*	4.6	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80103 +23°C*	13.3	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80103 -30°C*	11.2	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	5.2	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	4.5	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	10.8	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -30°C*	10.3	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80103 sp=62mm*	5.6	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80103 sp=62mm*	5.1	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80103 sp=62mm*	13.3	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80103 sp=62mm*	10.4	kJ/m²	ISO 179/1eU
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	5.1	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	4.4	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	12	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80104 sp=62mm*	8.7	kJ/m²	ISO 179/1eU
Instrumented Dart Impact Total Energy, 23°C	7.3	J	ASTM D3763
Instrumented Dart Impact Energy @ peak, 23°C	4.2	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	140 - 150	°C
Drying Time	4 - 6	Hrs
Melt Temperature	340 - 345	°C
Nozzle Temperature	340 - 350	°C
Front - Zone 3 Temperature	340 - 350	°C
Middle - Zone 2 Temperature	330 - 340	°C
Rear - Zone 1 Temperature	280 - 300	°C
Mold Temperature	100 - 120	°C
Back Pressure	0.1 - 0.4	MPa
Screw Speed	80 - 100	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	90	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	1.8	%	ASTM D638
Tensile Modulus, 5 mm/min	13950	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	130	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	14200	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	77	MPa	ISO 527
Tensile Strain, break, 5 mm/min	1.6	%	ISO 527
Tensile Modulus, 1 mm/min	13450	MPa	ISO 527
Flexural Strength, 2 mm/min	110	MPa	ISO 178
Flexural Modulus, 2 mm/min	14300	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.78	-	ASTM D792
Water Absorption, (23°C/24hrs)	0.02	%	ISO 62-1
Melt Flow Rate
– 345°C/2.16 kgf	10	g/10 min	ASTM D1238
Mold Shrinkage, flow	0.1	%	SABIC method
Mold Shrinkage, xflow	0.2	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	280	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	252	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	280	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	254	°C	ISO 75/Af
CTE, 23°C to 150°C, flow	1.0E-05	1/°C	ASTM E831
CTE, 23°C to 150°C, xflow	4.0E-05	1/°C	ASTM E831
CTE, 23°C to 150°C, flow	0.5E-05	1/°C	ISO 11359-2
CTE, 23°C to 150°C, xflow	3.8E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	190	°C	ISO 306
Vicat Softening Temp, Rate B/120	193	°C	ISO 306
*Thermal Conductivity in-plane, 250.4mm disc**	9	W/m-K	ASTM E1461-07
*Thermal Conductivity through-plane, 10103mm sample*	2	W/m-K	ASTM E1461-07

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES