LNP KONDUIT OTF2B compound is based on Polyphenylene Sulfide (PPS) resin containing 10% glass fiber and 55% proprietary thermal fillers. Added features of this grade include: Thermally Conductive.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 0 | ≥3 | mm | UL 746A |
| Hot-Wire Ignition (HWI), PLC 2 | ≥1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 3 | ≥1.5 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 0 | PLC Code | UL 746A |
| Arc Resistance, Tungsten {PLC} | 4 | PLC Code | ASTM D495 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94V-0 Flame Class Rating | 1.5 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 170 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 16 | J/m | ASTM D256 |
| Izod Impact, unnotched 80*10*4 +23°C | 14 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 315 - 320 | °C | |
| Front - Zone 3 Temperature | 330 - 345 | °C | |
| Middle - Zone 2 Temperature | 320 - 330 | °C | |
| Rear - Zone 1 Temperature | 305 - 315 | °C | |
| Mold Temperature | 140 - 165 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 83 | MPa | ASTM D638 |
| Tensile Strain, break | 0.9 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 16370 | MPa | ASTM D638 |
| Flexural Stress | 136 | MPa | ASTM D790 |
| Flexural Modulus | 15610 | MPa | ASTM D790 |
| Tensile Stress, break | 84 | MPa | ISO 527 |
| Tensile Strain, break | 0.8 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 16250 | MPa | ISO 527 |
| Flexural Stress | 137 | MPa | ISO 178 |
| Flexural Modulus | 14850 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 2.208 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 0.5 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.7 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 0.45 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.71 | % | ISO 294 |
| Wear Factor Washer | 4141 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.51 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.52 | - | ASTM D3702 Modified: Manual |
| Density | 2.2 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Thermal Conductivity | 1.05 | W/m-°C | ASTM E1530 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 264 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 202 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 130 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 130 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 130 | °C | UL 746B |