ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | >2.5E+04 | Ω | ASTM D257 |
Comparative Tracking Index (UL) {PLC} | 4 | PLC Code | UL 746A |
Hot-Wire Ignition (HWI), PLC 0 | ≥1.2 | mm | UL 746A |
LNP KONDUIT OX10324 compound is based on Polyphenylene Sulfide (PPS) resin containing glass fiber and proprietary thermal filler. Added features of this grade include: Thermally Conductive and Non-Brominated, Non-Chlorinated Flame Retardant.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | >2.5E+04 | Ω | ASTM D257 |
Comparative Tracking Index (UL) {PLC} | 4 | PLC Code | UL 746A |
Hot-Wire Ignition (HWI), PLC 0 | ≥1.2 | mm | UL 746A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 70 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 24 | J/m | ASTM D256 |
Izod Impact, unnotched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 3 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 - 150 | °C | |
Drying Time | 4 | Hrs | |
Melt Temperature | 320 - 350 | °C | |
Front - Zone 3 Temperature | 315 - 345 | °C | |
Middle - Zone 2 Temperature | 315 - 345 | °C | |
Rear - Zone 1 Temperature | 315 - 345 | °C | |
Mold Temperature | 110 - 150 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 60 - 100 | rpm | |
Shot to Cylinder Size | 50 - 75 | % |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, brk, Type I, 5 mm/min | 49 | MPa | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 0.6 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 13500 | MPa | ASTM D638 |
Flexural Stress, brk, 1.3 mm/min, 50 mm span | 75 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 15600 | MPa | ASTM D790 |
Tensile Stress, break, 5 mm/min | 53 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 0.6 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 14000 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 73 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 13500 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Mold Shrinkage, flow, 24 hrs | 0.1 - 0.2 | % | ISO 294 |
Mold Shrinkage, xflow, 24 hrs | 0.1 - 0.3 | % | ISO 294 |
Density | 1.75 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/24hrs) | 0.01 | % | ISO 62-1 |
Water Absorption, 23°C/24hrs | 0.01 | % | SABIC method |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm | 275 | °C | ASTM D648 |
HDT, 1.82 MPa, 6.4 mm, unannealed | 258 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 1.32E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 2.5E-05 | 1/°C | ASTM E831 |
Thermal Conductivity through-plane, 60*60*3mm plaque | 1.3 | W/m-K | ISO 22007-2 |
Thermal Conductivity in-plane, 60*60*3mm plaque | 18 | W/m-K | ISO 22007-2 |
Thermal Conductivity through-plane, 10*10*3mm sample | 3.5 | W/m-K | ASTM E1461-07 |
Thermal Conductivity in-plane, 25*0.4mm disc | 15 | W/m-K | ASTM E1461-07 |
CTE, -30°C to 80°C, flow | 1.3E-05 | 1/°C | ISO 11359-2 |
CTE, -30°C to 80°C, xflow | 2.39E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 80°C, flow | 1.38E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 80°C, xflow | 2.44E-05 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 165°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 231 | °C | ISO 75/Af |
Relative Temp Index, Elec | 130 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 130 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 130 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.