LNP™ KONDUIT™ Compound OX11315

LNP KONDUIT OX11315 compound is based on Polyphenylene Sulfide (PPS) resin containing proprietary thermal filler. Added features of this grade include: Thermally Conductive, Electrically Insulative and Non-Brominated, Non-Chlorinated Flame Retardant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyphenylene Sulfide, Linear (PPS, Linear)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Flame Retardant
No PFAS intentionally added
Non Cl/Br flame retardant
Thermally Conductive
Thermally conductive/Electrically isolative

Industry

Material previously used in

Building Component
Electrical
Home Appliances
Lighting
Material Handling
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

LED Lighting
Non-LED Lighting
Swimming Pool/Spa

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Comparative Tracking Index	400	V	IEC 60112
Surface Resistivity	2.4E+15	Ω	ASTM D257
Dielectric Strength, 1.6 mm	1.2	kV/mm	IEC 60243-1

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Yellow Card Link 2	View	-	-
UL Recognized, 94-5VA Flame Class Rating	≥2.5	mm	UL 94
UL Recognized, 94V-0 Flame Class Rating	1	mm	UL 94
UV-light, water exposure/immersion	F1	-	UL 746C

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	54	J/m	ASTM D4812
Izod Impact, notched, 23°C	16	J/m	ASTM D256
Multiaxial Impact	1	J	ISO 6603
Instrumented Dart Impact Total Energy, 23°C	5	J	ASTM D3763
*Izod Impact, unnotched 80104 +23°C*	3	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	1	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120 - 150	°C
Drying Time	4	Hrs
Melt Temperature	320 - 350	°C
Front - Zone 3 Temperature	315 - 345	°C
Middle - Zone 2 Temperature	315 - 345	°C
Rear - Zone 1 Temperature	315 - 345	°C
Mold Temperature	110 - 150	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	60 - 100	rpm
Shot to Cylinder Size	50 - 75	%

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	41	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	0.2	%	ASTM D638
Tensile Modulus, 5 mm/min	30100	MPa	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	82	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	26500	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	54	MPa	ISO 527
Tensile Strain, break, 5 mm/min	0.3	%	ISO 527
Tensile Modulus, 1 mm/min	18380	MPa	ISO 527
Flexural Stress	84	MPa	ISO 178
Flexural Modulus, 2 mm/min	21380	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.78	-	ASTM D792
Density	1.76	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.01	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.34	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.44	%	ASTM D955
Moisture Absorption (23°C / 50% RH)	0.01	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	275	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	242	°C	ASTM D648
Specific Heat	1.26	J/g-°C	ASTM C351
*Thermal Conductivity through-plane, 10103mm sample*	3.5	W/m-K	ASTM E1461-07
*Thermal Conductivity in-plane, 250.4mm disc**	15	W/m-K	ASTM E1461-07
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	275	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	238	°C	ISO 75/Af
Relative Temp Index, Elec	130	°C	UL 746B
Relative Temp Index, Mech w/impact	130	°C	UL 746B
Relative Temp Index, Mech w/o impact	130	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES