LNP™ KONDUIT™ Compound PX10323

LNP KONDUIT PX10323 compound is based on Nylon 6 resin containing glass fiber and proprietary thermal filler. Added features of this grade include: Thermally Conductive.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyamide 6 (Nylon 6)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Asia
Europe

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

No PFAS intentionally added
Thermally Conductive

Industry

Material previously used in

Building Component
Electrical
Home Appliances
Lighting
Material Handling
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

LED Lighting

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.05E+06	Ω	ASTM D257

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Glow Wire Flammability Index 850°C, passes at	1	mm	IEC 60695-2-12
Glow Wire Flammability Index 960°C, passes at	1.6	mm	IEC 60695-2-12
Glow Wire Ignitability Temperature, 1.0 mm	825	°C	IEC 60695-2-13

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	73	J/m	ASTM D4812
Izod Impact, notched, 23°C	30	J/m	ASTM D256
*Izod Impact, unnotched 80104 +23°C*	6	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	3	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	270 - 295	°C
Front - Zone 3 Temperature	270 - 290	°C
Middle - Zone 2 Temperature	270 - 290	°C
Rear - Zone 1 Temperature	260 - 275	°C
Mold Temperature	85 - 100	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	20 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	70	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	0.9	%	ASTM D638
Tensile Modulus, 5 mm/min	13700	MPa	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	96	MPa	ASTM D790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	95	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	14200	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	73	MPa	ISO 527
Tensile Strain, break, 5 mm/min	0.8	%	ISO 527
Tensile Modulus, 1 mm/min	14000	MPa	ISO 527
Flexural Stress, break, 2 mm/min	96	MPa	ISO 178
Flexural Modulus, 2 mm/min	14300	MPa	ISO 178
Impact Strength	3.7 - 6.8	kJ/m²	ISO R179

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.61	g/cm³	ASTM D792
Mold Shrinkage, flow, 24 hrs	0.2	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.22	%	ASTM D955
Moisture Absorption (23°C / 50% RH)	0.04	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 6.4 mm, unannealed	204	°C	ASTM D648
CTE, 40°C to 120°C, flow	1.24E-05	1/°C	ASTM E831
CTE, 40°C to 120°C, xflow	7.27E-05	1/°C	ASTM E831
*Thermal Conductivity through-plane, 60603mm plaque*	1.5	W/m-K	ISO 22007-2
*Thermal Conductivity in-plane, 60603mm plaque*	18	W/m-K	ISO 22007-2
*Thermal Conductivity through-plane, 10103mm sample*	3.5	W/m-K	ASTM E1461-07
*Thermal Conductivity in-plane, 250.4mm disc**	15	W/m-K	ASTM E1461-07
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	217	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	201	°C	ISO 75/Af

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.05E+06	Ω	ASTM D257

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94HB Flame Class Rating	≥0.75	mm	UL 94
Glow Wire Flammability Index, 1.0 mm	960	°C	IEC 60695-2-12
Glow Wire Flammability Index, 1.5 mm	960	°C	IEC 60695-2-12
Glow Wire Flammability Index, 3.0 mm	960	°C	IEC 60695-2-12
Glow Wire Ignitability Temperature, 1.0 mm	825	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 1.5 mm	850	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 3.0 mm	960	°C	IEC 60695-2-13

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	73	J/m	ASTM D4812
Izod Impact, notched, 23°C	30	J/m	ASTM D256
*Izod Impact, unnotched 80104 +23°C*	6	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	3	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80 - 90	°C
Drying Time	3 - 4	Hrs
Melt Temperature	270 - 300	°C
Nozzle Temperature	270 - 300	°C
Front - Zone 3 Temperature	270 - 300	°C
Middle - Zone 2 Temperature	270 - 300	°C
Rear - Zone 1 Temperature	260 - 290	°C
Mold Temperature	80 - 100	°C
Back Pressure	3 - 9	MPa
Screw Speed	30 - 150	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	70	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	0.9	%	ASTM D638
Tensile Modulus, 5 mm/min	13700	MPa	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	95	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	14200	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	73	MPa	ISO 527
Tensile Strain, break, 5 mm/min	0.8	%	ISO 527
Tensile Modulus, 1 mm/min	14000	MPa	ISO 527
Flexural Stress, break, 2 mm/min	96	MPa	ISO 178
Flexural Modulus, 2 mm/min	14300	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.61	g/cm³	ASTM D792
Mold Shrinkage, flow, 24 hrs	0.2	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.22	%	ASTM D955
Density	1.61	g/cm³	ISO 1183

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	186	°C	ASTM D648
CTE, -40°C to 40°C, flow	1.61E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	3.56E-05	1/°C	ASTM E831
*Thermal Conductivity in-plane, 250.4mm disc**	15	W/m-K	ASTM E1461-07
*Thermal Conductivity through-plane, 10103mm sample*	3.5	W/m-K	ASTM E1461-07
*Thermal Conductivity in-plane, 60603mm plaque*	18	W/m-K	ISO 22007-2
*Thermal Conductivity through-plane, 60603mm plaque*	1.5	W/m-K	ISO 22007-2
CTE, -30°C to 80°C, flow	1.4E-05	1/°C	ISO 11359-2
CTE, -30°C to 80°C, xflow	3.95E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, flow	1.62E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	4.77E-05	1/°C	ISO 11359-2
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	201	°C	ISO 75/Af
Ball Pressure Test, approximate maximum	205	°C	IEC 60695-10-2
Ball Pressure Test, 165°C +/- 2°C	PASSES	-	IEC 60695-10-2

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES

LNP™ KONDUIT™ Compound PX10323

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL