LNP KONDUIT PX11311U compound is based on Nylon 6 resin containing mineral and glass fiber. Added features of this grade include: Thermally Conductive, Electrically Insulative, Improved UV Stability and Non-Brominated, Non-Chlorinated Flame Retardant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+16 | Ω | ASTM D257 |
| Dielectric Strength, in oil, 1.6 mm | 15.9 | kV/mm | ASTM D149 |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Hot-Wire Ignition (HWI), PLC 0 | ≥1 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | ≥1 | mm | UL 746A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94V-0 Flame Class Rating | ≥1 | mm | UL 94 |
| Glow Wire Ignitability Temperature, 1.0 mm | 800 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 1.5 mm | 775 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 1.6 mm | 775 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 3.0 mm | 800 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index, 3.0 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 1.5 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 1.0 mm | 960 | °C | IEC 60695-2-12 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 25 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 3 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 270 - 295 | °C | |
| Front - Zone 3 Temperature | 270 - 290 | °C | |
| Middle - Zone 2 Temperature | 270 - 290 | °C | |
| Rear - Zone 1 Temperature | 260 - 275 | °C | |
| Mold Temperature | 85 - 100 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 20 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 5 mm/min | 105 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 12000 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 170 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 11000 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage, flow, 24 hrs | 0.45 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.65 | % | ISO 294 |
| Density | 1.74 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/24hrs) | 0.36 | % | ISO 62-1 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm | 209 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 3.08E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 4.77E-05 | 1/°C | ASTM E831 |
| Thermal Conductivity through-plane, 60*60*3mm plaque | 0.8 | W/m-K | ISO 22007-2 |
| Thermal Conductivity in-plane, 60*60*3mm plaque | 1.5 | W/m-K | ISO 22007-2 |
| CTE, -30°C to 80°C, flow | 3.46E-05 | 1/°C | ISO 11359-2 |
| CTE, -30°C to 80°C, xflow | 6.04E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, flow | 3.72E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 7.34E-05 | 1/°C | ISO 11359-2 |
| Thermal Conductivity through-plane, ?80*3mm discs | 1.1 | W/m-K | ISO 22007-2 |
| Thermal Conductivity in-plane, ?80*3mm discs | 1.3 | W/m-K | ISO 22007-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Ball Pressure Test, 165°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/120 | 205 | °C | ISO 306 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 208 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 185 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 120 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 110 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 130 | °C | UL 746B |