LNP KONDUIT PX13012 compound is based on Nylon 6 resin containing proprietary thermal filler. Added features of this grade include: Thermally Conductive, Electrically Insulative and Non-Brominated, Non-Chlorinated Flame Retardant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 4.E+14 | Ω | ASTM D257 |
| Dielectric Strength, in oil, 1.6 mm | 7.2 | kV/mm | ASTM D149 |
| Dielectric Strength, 1.6 mm | 6.1 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Hot-Wire Ignition (HWI), PLC 0 | ≥0.8 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | ≥0.8 | mm | UL 746A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94V-0 Flame Class Rating | ≥0.8 | mm | UL 94 |
| Glow Wire Ignitability Temperature, 0.8 mm | 750 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 1.6 mm | 775 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 3.0 mm | 800 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index, 0.8 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 1.6 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 3.0 mm | 960 | °C | IEC 60695-2-12 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 152 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 15 | J/m | ASTM D256 |
| Izod Impact, unnotched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 3 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 270 - 295 | °C | |
| Front - Zone 3 Temperature | 270 - 290 | °C | |
| Middle - Zone 2 Temperature | 270 - 290 | °C | |
| Rear - Zone 1 Temperature | 260 - 275 | °C | |
| Mold Temperature | 85 - 100 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 20 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 68 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.2 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 10350 | MPa | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 119 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 11800 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 75 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 13000 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 105 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 12000 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage on Tensile Bar, flow | 0.7 | % | SABIC method |
| Mold Shrinkage, flow, 24 hrs | 0.55 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.65 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 0.55 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.65 | % | ISO 294 |
| Density | 1.68 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/24hrs) | 0.23 | % | ISO 62-1 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm | 203 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 137 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 3.3E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 4.4E-05 | 1/°C | ASTM E831 |
| Thermal Conductivity through-plane, 60*60*3mm plaque | 1.2 | W/m-K | ISO 22007-2 |
| Thermal Conductivity in-plane, 60*60*3mm plaque | 5.5 | W/m-K | ISO 22007-2 |
| CTE, -30°C to 80°C, flow | 3.9E-05 | 1/°C | ISO 11359-2 |
| CTE, -30°C to 80°C, xflow | 5.5E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 165°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 203 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 160 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 130 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 100 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 130 | °C | UL 746B |