LNP™ KONDUIT™ Compound PX13322

LNP KONDUIT PX13322 compound is based on Nylon 6 resin containing mineral and glass fiber. Added features of this grade include: Thermally Conductive, Electrically Insulative and Non-Brominated, Non-Chlorinated Flame Retardant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyamide 6 (Nylon 6)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Flame Retardant
No PFAS intentionally added
Non Cl/Br flame retardant
Thermally conductive/Electrically isolative

Industry

Material previously used in

Building Component
Electrical
Home Appliances
Lighting
Material Handling
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Electronic Components
Fog Lamp
LED Lighting
led
electronic component
burn-in test socket
bits
test socket
thermal conductive
lens folder
flash light
camera
wireless
heat sink
thermal management
thermal dissipation
thermistor
cooling fin
electronics housing
electric vehicle

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	>1.E+15	Ω	ASTM D257
Dielectric Strength, in oil, 1.0 mm	>10	kV/mm	ASTM D149
Dielectric Constant (Dk), 1.1 GHz	4.86	-	ASTM ES 7-83
Dissipation Factor (Df), 1.1 GHz	0.0103	-	ASTM ES 7-83
Comparative Tracking Index	600	V	IEC 60112
Hot-Wire Ignition (HWI), PLC 0	≥1	mm	UL 746A
Hot-Wire Ignition (HWI), PLC 1	≥0.8	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 0	≥0.8	mm	UL 746A

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	≥0.8	mm	UL 94
Glow Wire Ignitability Temperature, 1.0 mm	800	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 3.0 mm	850	°C	IEC 60695-2-13
Glow Wire Flammability Index, 1.0 mm	960	°C	IEC 60695-2-12
Glow Wire Flammability Index, 3.0 mm	960	°C	IEC 60695-2-12

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	235	J/m	ASTM D4812
Izod Impact, notched, 23°C	21	J/m	ASTM D256
*Izod Impact, unnotched 80104 +23°C*	16	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	3	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	270 - 295	°C
Front - Zone 3 Temperature	270 - 290	°C
Middle - Zone 2 Temperature	270 - 290	°C
Rear - Zone 1 Temperature	260 - 275	°C
Mold Temperature	85 - 100	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	20 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	77	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	0.7	%	ASTM D638
Tensile Modulus, 5 mm/min	13700	MPa	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	127	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	11000	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	78	MPa	ISO 527
Tensile Strain, break, 5 mm/min	0.8	%	ISO 527
Tensile Modulus, 1 mm/min	13000	MPa	ISO 527
Flexural Stress, break, 2 mm/min	128	MPa	ISO 178
Flexural Modulus, 2 mm/min	12000	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.69	g/cm³	ASTM D792
Mold Shrinkage, flow, 24 hrs	0.54	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.57	%	ASTM D955
Water Absorption, (23°C/24hrs)	0.06	%	ISO 62-1

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm	205	°C	ASTM D648
HDT, 1.82 MPa, 6.4 mm, unannealed	174	°C	ASTM D648
CTE, -40°C to 40°C, flow	3.08E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	4.77E-05	1/°C	ASTM E831
CTE, 40°C to 120°C, flow	2.35E-05	1/°C	ASTM E831
CTE, 40°C to 120°C, xflow	5.25E-05	1/°C	ASTM E831
*Thermal Conductivity through-plane, 60603mm plaque*	1	W/m-K	ISO 22007-2
*Thermal Conductivity in-plane, 60603mm plaque*	3.3	W/m-K	ISO 22007-2
*Thermal Conductivity through-plane, 10103mm sample*	2	W/m-K	ASTM E1461-07
*Thermal Conductivity in-plane, 250.4mm disc**	3.4	W/m-K	ASTM E1461-07
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	204	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	162	°C	ISO 75/Af
Relative Temp Index, Elec	65	°C	UL 746B
Relative Temp Index, Mech w/impact	65	°C	UL 746B
Relative Temp Index, Mech w/o impact	65	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES