LNP™ LUBRICOMP™ Compound 2FL24

LNP LUBRICOMP 2FL24 compound is based on Ethylene Tetrafluoroethylene (ETFE) resin containing 20% glass fiber and 10% PTFE. Added features of this grade include: Wear Resistant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Ethylene Tetrafluoroethylene Copolymer (ETFE)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Wear resistant

Industry

Material previously used in

Electronic Components
Energy Management
Material Handling

Applications

Possible usage of material

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	1340	J/m	ASTM D4812
Izod Impact, notched, 23°C	488	J/m	ASTM D256
Multiaxial Impact	8	J	ISO 6603
Instrumented Dart Impact Total Energy, 23°C	20	J	ASTM D3763
*Izod Impact, unnotched 80104 +23°C*	92	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	45	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120 - 150	°C
Drying Time	4	Hrs
Melt Temperature	315	°C
Front - Zone 3 Temperature	325 - 340	°C
Middle - Zone 2 Temperature	300 - 325	°C
Rear - Zone 1 Temperature	280 - 300	°C
Mold Temperature	90 - 120	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	69	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	6.5	%	ASTM D638
Tensile Modulus, 5 mm/min	6440	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	4760	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	67	MPa	ISO 527
Tensile Strain, break, 5 mm/min	6.2	%	ISO 527
Tensile Modulus, 1 mm/min	5000	MPa	ISO 527
Flexural Strength, 2 mm/min	89	MPa	ISO 178
Flexural Modulus, 2 mm/min	4980	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.8	-	ASTM D792
Density	1.8	g/cm³	ASTM D792
Mold Shrinkage, flow, 24 hrs	0.6 - 0.8	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	1 - 3	%	ASTM D955
Moisture Absorption (23°C / 50% RH)	0.01	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	251	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	198	°C	ASTM D648
CTE, -30°C to 30°C, flow	2.4E-05	1/°C	ASTM D696
CTE, -30°C to 30°C, xflow	9.4E-05	1/°C	ASTM D696
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	239	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	160	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES