LNP™ LUBRICOMP™ Compound 2X00858

LNP LUBRICOMP 2X00858 compound is based on Fluorinated ethylene propylene (FEP) resin containing proprietary fillers. Added features of this grade include: Wear Resistant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Fluorinated Ethylene Propylene (FEP)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Wear resistant

Industry

Material previously used in

Electronic Components
Energy Management
Material Handling

Applications

Possible usage of material

Document Handling

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Compliant, 94V-0 Flame Class Rating	1.5	mm	UL 94 by SABIC-IP

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	981	J/m	ASTM D4812
Izod Impact, notched, 23°C	683	J/m	ASTM D256
*Izod Impact, unnotched 80104 +23°C*	84	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	31	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120 - 150	°C
Drying Time	4	Hrs
Melt Temperature	370 - 390	°C
Front - Zone 3 Temperature	380 - 400	°C
Middle - Zone 2 Temperature	380 - 400	°C
Rear - Zone 1 Temperature	360 - 380	°C
Mold Temperature	200 - 220	°C
Back pressure (Plastic Pressure)	2.5 - 2.9	MPa

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	14	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	12	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	5.5	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	9.3	%	ASTM D638
Tensile Modulus, 50 mm/min	1010	MPa	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	20	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	790	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	14	MPa	ISO 527
Tensile Stress, break, 5 mm/min	13	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	6.1	%	ISO 527
Tensile Strain, break, 5 mm/min	9.3	%	ISO 527
Tensile Modulus, 1 mm/min	930	MPa	ISO 527
Flexural Stress	19	MPa	ISO 178
Flexural Modulus, 2 mm/min	870	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	2.17	-	ASTM D792
Density	2.17	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.01	%	ASTM D570

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	79	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	57	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	80	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	61	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES