LNP™ LUBRICOMP™ Compound 9X06483

LNP LUBRICOMP 9X06483 compound is based on a Nylon 4/6 resin containing PTFE. Added features of this grade include: Wear Resistant, Heat Stabilized.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyamide 46 (Nylon 46)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Heat Stabilized
Wear resistant

Industry

Material previously used in

Automotive Under the Hood
Commercial Appliance
Electronic Components
Home Appliances
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Auto Aftermarket

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	924	J/m	ASTM D4812
Izod Impact, notched, 23°C	52	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	3	J	ASTM D3763
*Izod Impact, unnotched 80104 +23°C*	56	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	5	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	40	Hrs
Maximum Moisture Content	0.05	%
Melt Temperature	310 - 320	°C
Front - Zone 3 Temperature	310 - 320	°C
Middle - Zone 2 Temperature	300 - 310	°C
Rear - Zone 1 Temperature	280 - 295	°C
Mold Temperature	80 - 120	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	80	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	74	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	5.8	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	5.9	%	ASTM D638
Tensile Modulus, 5 mm/min	3130	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	2960	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	78	MPa	ISO 527
Tensile Stress, break, 5 mm/min	76	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	6.5	%	ISO 527
Tensile Strain, break, 5 mm/min	6.6	%	ISO 527
Tensile Modulus, 1 mm/min	3000	MPa	ISO 527
Flexural Strength, 2 mm/min	101	MPa	ISO 178
Flexural Modulus, 2 mm/min	2800	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.29	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	1.8	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	1 - 3	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	2 - 4	%	ASTM D955
Wear Factor Washer	11	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Wear Factor Ring	-1	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF	0.32	-	ASTM D3702 Modified: Manual
Static COF	0.32	-	ASTM D3702 Modified: Manual
Density	1.28	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	2.7	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	283	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	151	°C	ASTM D648
CTE, -30°C to 30°C, xflow	9.3E-05	1/°C	ASTM D696
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	276	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	92	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES