LNP™ LUBRICOMP™ Compound CG006

LNP LUBRICOMP CG006 compound is based on Polystyrene (PS) resin containing graphite. Added features of this grade include: Wear Resistant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polystyrene (PS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

No PFAS intentionally added
Wear resistant

Industry

Material previously used in

Building Component
Water Management

Applications

Possible usage of material

Meter Gas
Meter Water
wobble plate
nutating plate
impellor

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, unnotched 80104 +23°C*	10	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	2	kJ/m²	ISO 180/1A
Charpy Impact, unnotched, 23°C	6.5	kJ/m²	ISO 179/2C
Charpy Impact, notched, 23°C	1.2	kJ/m²	ISO 179/2C
*Charpy 23°C, Unnotch Edgew 80103 sp=62mm*	6.5	kJ/m²	ISO 179/1eU
*Charpy 23°C, V-notch Edgew 80103 sp=62mm*	1.2	kJ/m²	ISO 179/1eA
Izod Impact, unnotched, 23°C	80	J/m	ASTM D4812
Izod Impact, notched, 23°C	12	J/m	ASTM D256

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.02	%
Drying Time (Cumulative)	48	Hrs
Melt Temperature	250	°C
Front - Zone 3 Temperature	265 - 275	°C
Middle - Zone 2 Temperature	245 - 255	°C
Rear - Zone 1 Temperature	220 - 230	°C
Mold Temperature	40 - 65	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break, 5 mm/min	45	MPa	ISO 527
Tensile Strain, break, 5 mm/min	1.3	%	ISO 527
Tensile Modulus, 1 mm/min	6200	MPa	ISO 527
Flexural Stress, break, 2 mm/min	72	MPa	ISO 178
Flexural Modulus, 2 mm/min	5400	MPa	ISO 178
Tensile Stress, brk, Type I, 5 mm/min	6600	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	1.2	%	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	74	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2100	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Mold Shrinkage on Tensile Bar, flow	0.1 - 0.3	%	SABIC method
Wear Factor Washer	799	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Instr.
Dynamic COF	0.3	-	ASTM D3702 Modified: Instr.
Static COF	0.55	-	ASTM D3702 Modified: Instr.
Density	1.22	g/cm³	ISO 1183

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Vicat Softening Temp, Rate B/50	99	°C	ISO 306
Vicat Softening Temp, Rate B/120	101	°C	ISO 306
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	89	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	97	°C	ISO 75/Bf

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES