IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 2 | kJ/m² | ISO 180/1A |
LNP LUBRICOMP CGI11XP compound is based on Polystyrene (PS) resin containing graphite. Added features of this grade include: Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 2 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 | Hrs | |
Melt Temperature | 250 | °C | |
Front - Zone 3 Temperature | 265 - 275 | °C | |
Middle - Zone 2 Temperature | 245 - 255 | °C | |
Rear - Zone 1 Temperature | 220 - 230 | °C | |
Mold Temperature | 40 - 65 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break, 5 mm/min | 46 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 2.7 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 3300 | MPa | ISO 527 |
Flexural Modulus, 2 mm/min | 3100 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Mold Shrinkage, flow | 0.3 | % | SABIC method |
Density | 1.07 | g/cm³ | ISO 1183 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 80 | °C | ISO 75/Af |