LNP LUBRICOMP DCI06APW compound is based on Polycarbonate (PC) resin containing 30% carbon fiber and silicone. Added features of this grade include: Electrically Conductive, High Flow, Wear Resistant. Healthcare, Biocompatible (ISO10993).
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+03 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 504 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 94 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 16 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 33 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 290 - 300 | °C | |
| Front - Zone 3 Temperature | 285 - 300 | °C | |
| Middle - Zone 2 Temperature | 275 - 290 | °C | |
| Rear - Zone 1 Temperature | 270 - 285 | °C | |
| Mold Temperature | 100 - 120 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 40 - 80 | rpm | |
| Maximum Moisture Content | 0.02 | % |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 183 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.4 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 25440 | MPa | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 265 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 20100 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 183 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.6 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 23830 | MPa | ISO 527 |
| Flexural Strength, 2 mm/min | 262 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 20600 | MPa | ISO 178 |
| Compressive Strength | 128 | MPa | SABIC method |
| Shear Modulus | 3508 | MPa | ASTM D732 |
| Shear Strength | 92 | MPa | ASTM D732 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Wear Factor Washer | 13 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.24 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.22 | - | ASTM D3702 Modified: Manual |
| Specific Gravity | 1.3 | - | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.11 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.05 - 0.15 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.15 - 0.4 | % | ASTM D955 |
| Melt Volume Rate, MVR at 300°C/5.0 kg | 28 | cm³/10 min | ASTM D1238 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 128 | °C | ASTM D648 |
| CTE, -30°C to 30°C, flow | 9.7E-06 | 1/°C | ASTM D696 |
| CTE, -30°C to 30°C, xflow | 4.6E-05 | 1/°C | ASTM D696 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 130 | °C | ISO 75/Af |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature