LNP LUBRICOMP DFL22ER compound is based on Polycarbonate (PC) resin containing 10% glass fiber and 10% PTFE. Added features of this grade include: Wear Resistant, Easy Molding, Mold Release.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 736 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 144 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy @ peak, 23°C | 23 | J | ASTM D3763 |
| Multiaxial Impact | 6 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 48 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 13 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 305 - 325 | °C | |
| Front - Zone 3 Temperature | 320 - 330 | °C | |
| Middle - Zone 2 Temperature | 310 - 320 | °C | |
| Rear - Zone 1 Temperature | 295 - 305 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield | 71 | MPa | ASTM D638 |
| Tensile Stress, break | 67 | MPa | ASTM D638 |
| Tensile Strain, yield | 3.3 | % | ASTM D638 |
| Tensile Strain, break | 5.5 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 4130 | MPa | ASTM D638 |
| Flexural Modulus | 4130 | MPa | ASTM D790 |
| Tensile Stress, yield | 71 | MPa | ISO 527 |
| Tensile Stress, break | 67 | MPa | ISO 527 |
| Tensile Strain, yield | 3.3 | % | ISO 527 |
| Tensile Strain, break | 5.8 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 4150 | MPa | ISO 527 |
| Flexural Stress | 118 | MPa | ISO 178 |
| Flexural Modulus | 3900 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.1 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.4 - 0.6 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.6 - 0.8 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 0.5 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.65 | % | ISO 294 |
| Wear Factor Washer | 165 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.37 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.43 | - | ASTM D3702 Modified: Manual |
| Density | 1.33 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 145 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 140 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 5.58E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 5.58E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 5.6E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 5.6E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 146 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 140 | °C | ISO 75/Af |