LNP™ LUBRICOMP™ Compound DFL36

LNP LUBRICOMP DFL36 compound is based on Polycarbonate (PC) resin containing 30% glass fiber, 15% PTFE. Added features of this grade include: Wear Resistant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

High stiffness/Strength
Wear resistant

Industry

Material previously used in

Building Component
Commercial Appliance
Electrical
Home Appliances
Mobile Phone - Computer - Tablets
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Data Management
Displays
Document Handling
Electronic Components
Lab Ware and Clinical Diagnostics
Medical Device
Meter Water
Personal Computing
Photovoltaic Components
Plumbing
Small Appliance

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-1 Flame Class Rating	≥3	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	923	J/m	ASTM D4812
Izod Impact, notched, 23°C	197	J/m	ASTM D256
*Izod Impact, unnotched 80104 +23°C*	55	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	16	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	305 - 325	°C
Front - Zone 3 Temperature	320 - 330	°C
Middle - Zone 2 Temperature	310 - 320	°C
Rear - Zone 1 Temperature	295 - 305	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield	123	MPa	ASTM D638
Tensile Stress, break	123	MPa	ASTM D638
Tensile Strain, yield	2.6	%	ASTM D638
Tensile Strain, break	2.8	%	ASTM D638
Tensile Modulus, 5 mm/min	9580	MPa	ASTM D638
Flexural Stress	186	MPa	ASTM D790
Flexural Modulus	8610	MPa	ASTM D790
Tensile Stress, yield	118	MPa	ISO 527
Tensile Stress, break	118	MPa	ISO 527
Tensile Strain, yield	2.6	%	ISO 527
Tensile Strain, break	2.7	%	ISO 527
Tensile Modulus, 1 mm/min	9080	MPa	ISO 527
Flexural Stress	185	MPa	ISO 178
Flexural Modulus	8340	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.54	g/cm³	ASTM D792
Mold Shrinkage, flow, 24 hrs	0.2 - 0.3	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.5	%	ASTM D955
Wear Factor Washer	22	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF	0.46	-	ASTM D3702 Modified: Manual
Static COF	0.41	-	ASTM D3702 Modified: Manual

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	143	°C	ASTM D648

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-1 Flame Class Rating	≥3	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, unnotched 80104 +23°C*	55	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	16	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	305 - 325	°C
Front - Zone 3 Temperature	320 - 330	°C
Middle - Zone 2 Temperature	310 - 320	°C
Rear - Zone 1 Temperature	295 - 305	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break, 5 mm/min	120	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.7	%	ISO 527
Flexural Stress, yield, 2 mm/min	199	MPa	ISO 178
Flexural Strain, break, 2 mm/min	3.1	%	ISO 178
Flexural Modulus, 2 mm/min	8600	MPa	ISO 178
Flexural Strain, break, 2 mm/min, 60°C	3.1	%	ISO 178
Flexural Strain, break, 2 mm/min, 100°C	3.5	%	ISO 178
Flexural Strain, break, 2 mm/min, 120°C	3.8	%	ISO 178
Flexural Stress, yield, 2 mm/min, 60°C	172	MPa	ISO 178
Flexural Stress, yield, 2 mm/min, 100°C	136	MPa	ISO 178
Flexural Stress, yield, 2 mm/min, 120°C	114	MPa	ISO 178
Flexural Modulus, 2 mm/min, 60°C	8400	MPa	ISO 178
Flexural Modulus, 2 mm/min, 100°C	8100	MPa	ISO 178
Flexural Modulus, 2 mm/min, 120°C	7500	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Mold Shrinkage on Tensile Bar, flow	0.1 - 0.3	%	SABIC method
Wear Factor Washer	22	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF	0.46	-	ASTM D3702 Modified: Manual
Static COF	0.41	-	ASTM D3702 Modified: Manual
Density	1.54	g/cm³	ISO 1183
Melt Volume Rate, MVR at 300°C/5.0 kg	8 - 12	cm³/10 min	ISO 1133

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
CTE, 23°C to 60°C, flow	2.4E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	7.6E-05	1/°C	ISO 11359-2
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	130	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES

LNP™ LUBRICOMP™ Compound DFL36

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL