LNP LUBRICOMP DL002 compound is based on Polycarbonate (PC) resin containing 10% PTFE. Added features of this grade include: Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | NB | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 240 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 300 - 315 | °C | |
| Front - Zone 3 Temperature | 310 - 320 | °C | |
| Middle - Zone 2 Temperature | 305 - 315 | °C | |
| Rear - Zone 1 Temperature | 295 - 305 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 53 | MPa | ASTM D638 |
| Tensile Strain, break | 53 | % | ASTM D638 |
| Flexural Stress | 81 | MPa | ASTM D790 |
| Flexural Modulus | 2270 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 0.7 - 0.9 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.7 - 0.9 | % | ASTM D955 |
| Wear Factor Washer | 97 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.28 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.17 | - | ASTM D3702 Modified: Manual |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 128 | °C | ASTM D648 |