LNP™ LUBRICOMP™ Compound DX09407H

LNP LUBRICOMP DX09407H compound is based on High Heat Polycarbonate (PC) resin containing proprietary additive. Added features of this grade include: Wear Resistant, Healthcare.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Healthcare/Formula lock
Wear resistant

Industry

Material previously used in

General Healthcare
Industrial Packaging
Patient Testing
Pharmaceutical Packaging and Drug Delivery
Surgical devices

Applications

Possible usage of material

Pharmaceutical Manufacturing

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	2214	J/m	ASTM D4812
Izod Impact, notched, 23°C	139	J/m	ASTM D256
*Izod Impact, unnotched 80104 +23°C*	191	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	11	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	3 - 4	Hrs
Drying Time (Cumulative)	48	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	295 - 315	°C
Nozzle Temperature	290 - 310	°C
Front - Zone 3 Temperature	295 - 315	°C
Middle - Zone 2 Temperature	280 - 305	°C
Rear - Zone 1 Temperature	270 - 295	°C
Mold Temperature	70 - 95	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.025 - 0.076	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	64	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	53	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	6.8	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	68	%	ASTM D638
Tensile Modulus, 5 mm/min	2230	MPa	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	90	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2300	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	64	MPa	ISO 527
Tensile Stress, break, 5 mm/min	56	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	6.9	%	ISO 527
Tensile Strain, break, 5 mm/min	111	%	ISO 527
Tensile Modulus, 1 mm/min	2130	MPa	ISO 527
Flexural Strain, break, 2 mm/min	76.8	%	ISO 178
Flexural Modulus, 2 mm/min	2080	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.21	-	ASTM D792
Mold Shrinkage, flow, 24 hrs	0.5 - 0.7	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.6 - 0.8	%	ASTM D955
Moisture Absorption (23°C / 50% RH)	0.21	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	139	°C	ASTM D648
CTE, -40°C to 40°C, flow	7.4E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	7.7E-05	1/°C	ISO 11359-2
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	137	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES