LNP™ LUBRICOMP™ Compound DX19519H

LNP LUBRICOMP DX19519H compound is based on Polycarbonate (PC) copolymer resin containing proprietary fillers. Added features of this grade include: Healthcare, Wear Resistant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Healthcare/Formula lock
Wear resistant

Industry

Material previously used in

General Healthcare
Industrial Packaging
Patient Testing
Pharmaceutical Packaging and Drug Delivery
Surgical devices

Applications

Possible usage of material

Surgical Devices
medical connector
drug connector

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, -30°C	156	J/m	ASTM D256
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	223.51	kJ/m²	ISO 179/1eU
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	43.79	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	16.86	kJ/m²	ISO 179/1eA
*Charpy -30°C, Unnotch Edgew 80104 sp=62mm*	304.27	kJ/m²	ISO 179/1eU
*Izod Impact, notched 80104 -30°C*	16.09	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 -30°C*	28.62	kJ/m²	ISO 180/1U
Izod Impact, notched, 23°C	614	J/m	ASTM D256
*Izod Impact, unnotched 80104 +23°C*	168.55	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	44.75	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Time	3 - 4	Hrs
Drying Time (Cumulative)	48	Hrs
Nozzle Temperature	290 - 310	°C
Vent Depth	0.025 - 0.076	mm
Drying Temperature	120	°C
Maximum Moisture Content	0.02	%
Melt Temperature	295 - 315	°C
Front - Zone 3 Temperature	295 - 315	°C
Middle - Zone 2 Temperature	280 - 305	°C
Rear - Zone 1 Temperature	270 - 295	°C
Mold Temperature	70 - 95	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	40 - 60	%

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 50 mm/min	2135	MPa	ASTM D638
Tensile Stress, yld, Type I, 50 mm/min	57.65	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	45.85	MPa	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	45.86	%	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	5.97	%	ASTM D638
Tensile Stress, yield, 50 mm/min	57.69	MPa	ISO 527
Tensile Stress, break, 50 mm/min	45.24	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5.9	%	ISO 527
Tensile Strain, break, 50 mm/min	45.24	%	ISO 527
Flexural Modulus, 1.3 mm/min, 50 mm span	2085	MPa	ASTM D790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	79	MPa	ASTM D790
Tensile Modulus, 1 mm/min	2091.4	MPa	ISO 527
Flexural Modulus, 2 mm/min	2160	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Melt Flow Rate, 300°C/1.2 kgf	27.7	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 300°C/1.2 kg	24.5	cm³/10 min	ASTM D1238
Melt Volume Rate, MVR at 300°C/1.2 kg	24.19	cm³/10 min	ISO 1133
Water Absorption, (23°C/24hrs)	0.07	%	ISO 62-1
Specific Gravity	1.2	-	ASTM D792
Mold Shrinkage, flow, 24 hrs	0.83	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.94	%	ASTM D955
Wear Factor Washer	211.5	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF	0.3495	-	ASTM D3702 Modified: Manual
Moisture Absorption (23°C / 50% RH)	0.28	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
CTE, -40°C to 95°C, flow	7.53E-05	1/°C	ASTM E831
CTE, -40°C to 95°C, xflow	7.51E-05	1/°C	ASTM E831
CTE, 23°C to 80°C, flow	8.08E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	7.95E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	145.95	°C	ISO 306
HDT, 1.82 MPa, 3.2mm, unannealed	123	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	119.8	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES