ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A |
Hot-Wire Ignition (HWI), PLC 1 | ≥3 | mm | UL 746A |
LNP LUBRICOMP DX96651 compound is based on Polycarbonate (PC) resin containing proprietary fillers. Added features of this grade include: Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A |
Hot-Wire Ignition (HWI), PLC 1 | ≥3 | mm | UL 746A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | NB | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 101 | J/m | ASTM D256 |
Instrumented Dart Impact Energy @ peak, 23°C | 41 | J | ASTM D3763 |
Multiaxial Impact | 128 | J | ISO 6603 |
Izod Impact, unnotched 80*10*4 +23°C | 137 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 300 - 315 | °C | |
Front - Zone 3 Temperature | 310 - 320 | °C | |
Middle - Zone 2 Temperature | 305 - 315 | °C | |
Rear - Zone 1 Temperature | 295 - 305 | °C | |
Mold Temperature | 80 - 110 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield | 48 | MPa | ASTM D638 |
Tensile Stress, break | 58 | MPa | ASTM D638 |
Tensile Modulus, 50 mm/min | 2200 | MPa | ASTM D638 |
Flexural Stress | 93 | MPa | ASTM D790 |
Flexural Modulus | 2480 | MPa | ASTM D790 |
Tensile Stress, yield | 55 | MPa | ISO 527 |
Tensile Stress, break | 46 | MPa | ISO 527 |
Tensile Modulus, 1 mm/min | 2400 | MPa | ISO 527 |
Flexural Stress | 90 | MPa | ISO 178 |
Flexural Modulus | 2600 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.23 | g/cm³ | ASTM D792 |
Moisture Absorption, (23°C/50% RH/24 hrs) | 0.16 | % | ASTM D570 |
Mold Shrinkage, flow, 24 hrs | 0.7 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 0.7 | % | ASTM D955 |
Mold Shrinkage, flow, 24 hrs | 0.73 | % | ISO 294 |
Mold Shrinkage, xflow, 24 hrs | 0.75 | % | ISO 294 |
Density | 1.23 | g/cm³ | ISO 1183 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 140 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 127 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 6.55E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 6.58E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 6.55E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 6.6E-05 | 1/°C | ISO 11359-2 |
Relative Temp Index, Elec | 80 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |