LNP LUBRICOMP DX99699 compound is based on Polycarbonate (PC) resin containing glass fiber and PTFE. Added features of this grade include: Wear Resistant, Mold Release
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 420 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 127 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 305 - 325 | °C | |
| Front - Zone 3 Temperature | 320 - 330 | °C | |
| Middle - Zone 2 Temperature | 310 - 320 | °C | |
| Rear - Zone 1 Temperature | 295 - 305 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 103 | MPa | ASTM D638 |
| Tensile Strain, break | 3 - 4 | % | ASTM D638 |
| Flexural Stress | 124 | MPa | ASTM D790 |
| Flexural Modulus | 5170 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.4 | - | ASTM D792 |
| Water Absorption, (23°C/24hrs) | 0.08 | % | ASTM D570 |
| Mold Shrinkage, flow, 3.2 mm | 0.25 - 0.35 | % | SABIC method |
| Matrix Tg | 149 | °C | DMA |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 10 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 6.4 mm, unannealed | 145 | °C | ASTM D648 |