LNP™ LUBRICOMP™ Compound ECL36

LNP LUBRICOMP ECL36 compound is based on Polyetherimide (PEI) resin containing 30% carbon fiber, 15% PTFE. Added features of this grade include: Wear Resistant, Electrically Conductive.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyetherimide (PEI)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Carbon fiber filled
Electrically Conductive
High stiffness/Strength
High temperature resistance
Wear resistant

Industry

Material previously used in

Building Component
Commercial Appliance
Electrical
Home Appliances
Mobile Phone - Computer - Tablets
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Enclosure/Housing/Cover

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+01 - 1.E+06	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	267	J/m	ASTM D4812
Izod Impact, notched, 23°C	42	J/m	ASTM D256
*Izod Impact, unnotched 80104 +23°C*	18	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	5	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	150	°C
Drying Time	4 - 6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	360 - 375	°C
Rear - Zone 1 Temperature	355 - 365	°C
Middle - Zone 2 Temperature	360 - 370	°C
Front - Zone 3 Temperature	365 - 375	°C
Nozzle Temperature	365 - 375	°C
Mold Temperature	140 - 180	°C
Back Pressure	0.3 - 0.7	MPa
Screw speed (Circumferential speed)	0.2 - 0.3	m/s
Vent Depth	0.025 - 0.076	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break	179	MPa	ASTM D638
Tensile Strain, break	1.7	%	ASTM D638
Flexural Stress	230	MPa	ASTM D790
Flexural Modulus	19160	MPa	ASTM D790
Tensile Stress, break	160	MPa	ISO 527
Tensile Strain, break	1.2	%	ISO 527
Tensile Modulus, 1 mm/min	21600	MPa	ISO 527

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.48	g/cm³	ASTM D792
Mold Shrinkage, flow, 24 hrs	0.1 - 0.3	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.1 - 0.4	%	ASTM D955
Wear Factor Washer	31	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF	0.39	-	ASTM D3702 Modified: Manual
Static COF	0.48	-	ASTM D3702 Modified: Manual
Density	1.49	g/cm³	ISO 1183

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	208	°C	ASTM D648

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+01 - 1.E+06	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	267	J/m	ASTM D4812
Izod Impact, notched, 23°C	42	J/m	ASTM D256
*Izod Impact, unnotched 80104 +23°C*	18	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	5	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	150	°C
Drying Time	4 - 6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	360 - 375	°C
Rear - Zone 1 Temperature	355 - 365	°C
Middle - Zone 2 Temperature	360 - 370	°C
Front - Zone 3 Temperature	365 - 375	°C
Nozzle Temperature	365 - 375	°C
Mold Temperature	140 - 180	°C
Back Pressure	0.3 - 0.7	MPa
Screw speed (Circumferential speed)	0.2 - 0.3	m/s
Vent Depth	0.025 - 0.076	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break	179	MPa	ASTM D638
Tensile Strain, break	1.7	%	ASTM D638
Flexural Stress	230	MPa	ASTM D790
Flexural Modulus	19160	MPa	ASTM D790
Tensile Stress, break	160	MPa	ISO 527
Tensile Strain, break	1.2	%	ISO 527
Tensile Modulus, 1 mm/min	21600	MPa	ISO 527

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.48	g/cm³	ASTM D792
Mold Shrinkage, flow, 24 hrs	0.1 - 0.3	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.1 - 0.4	%	ASTM D955
Wear Factor Washer	31	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF	0.39	-	ASTM D3702 Modified: Manual
Static COF	0.48	-	ASTM D3702 Modified: Manual
Density	1.49	g/cm³	ISO 1183

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+01 - 1.E+06	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80103 -40°C*	7	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	18	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -40°C*	25	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	5	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	150	°C
Drying Time	4 - 6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	360 - 375	°C
Rear - Zone 1 Temperature	355 - 365	°C
Middle - Zone 2 Temperature	360 - 370	°C
Front - Zone 3 Temperature	365 - 375	°C
Nozzle Temperature	365 - 375	°C
Mold Temperature	140 - 180	°C
Back Pressure	0.3 - 0.7	MPa
Screw speed (Circumferential speed)	0.2 - 0.3	m/s
Vent Depth	0.025 - 0.076	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break, 5 mm/min	160	MPa	ISO 527
Tensile Strain, break, 5 mm/min	1.2	%	ISO 527
Tensile Modulus, 1 mm/min	21600	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	256	MPa	ISO 178
Flexural Strain, break, 2 mm/min	1.6	%	ISO 178
Flexural Modulus, 2 mm/min	18500	MPa	ISO 178
Flexural Strain, break, 2 mm/min, 80°C	1.5	%	ISO 178
Flexural Strain, break, 2 mm/min, 120°C	1.4	%	ISO 178
Flexural Strain, break, 2 mm/min, 150°C	1.6	%	ISO 178
Flexural Strain, break, 2 mm/min, 200°C	1	%	ISO 178
Flexural Stress, yield, 2 mm/min, 80°C	214	MPa	ISO 178
Flexural Stress, yield, 2 mm/min, 120°C	182	MPa	ISO 178
Flexural Stress, yield, 2 mm/min, 150°C	145	MPa	ISO 178
Flexural Stress, yield, 2 mm/min, 200°C	91	MPa	ISO 178
Flexural Modulus, 2 mm/min, 80°C	17900	MPa	ISO 178
Flexural Modulus, 2 mm/min, 120°C	17400	MPa	ISO 178
Flexural Modulus, 2 mm/min, 150°C	16400	MPa	ISO 178
Flexural Modulus, 2 mm/min, 200°C	15300	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Mold Shrinkage, flow, 24 hrs	0.25	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.1 - 0.4	%	ISO 294
Wear Factor Washer	31	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF	0.39	-	ASTM D3702 Modified: Manual
Static COF	0.48	-	ASTM D3702 Modified: Manual
Density	1.49	g/cm³	ISO 1183
Water Absorption, (23°C/24hrs)	0.32	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)	0.21	%	ISO 62
Melt Volume Rate, MVR at 345°C/10.0 kg	4 - 6	cm³/10 min	ISO 1133

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Heat	1890	J/kg-K	ASTM E1269
CTE, 23°C to 60°C, flow	9.E-06	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	2.8E-05	1/°C	ISO 11359-2
Thermal Conductivity	0.33	W/m-K	ASTM D5930

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES

LNP™ LUBRICOMP™ Compound ECL36

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

ELECTRICAL

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

ELECTRICAL

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

ELECTRICAL

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

Related Documents