LNP™ LUBRICOMP™ Compound EFL34HL

LNP LUBRICOMP EFL34HL compound is based on Polyetherimide (PEI) resin containing 20% glass fiber, 15% PTFE. Added features of this grade include: Wear Resistant, Low Extractable.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyetherimide (PEI)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Food contact
Healthcare/Formula lock
High temperature resistance
Wear resistant

Industry

Material previously used in

Food & Beverage
General Healthcare
Home Appliances
Industrial Packaging
Patient Testing
Pharmaceutical Packaging and Drug Delivery
Surgical devices
Water Management

Applications

Possible usage of material

Enclosure/Housing/Cover

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	480	J/m	ASTM D4812
Izod Impact, notched, 23°C	69	J/m	ASTM D256
Instrumented Dart Impact Energy @ peak, 23°C	8	J	ASTM D3763
Multiaxial Impact	2	J	ISO 6603
*Izod Impact, unnotched 80104 +23°C*	32	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	20	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	150	°C
Drying Time	4 - 6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	360 - 375	°C
Rear - Zone 1 Temperature	355 - 365	°C
Middle - Zone 2 Temperature	360 - 370	°C
Front - Zone 3 Temperature	365 - 375	°C
Nozzle Temperature	365 - 375	°C
Mold Temperature	140 - 180	°C
Back Pressure	0.3 - 0.7	MPa
Screw speed (Circumferential speed)	0.2 - 0.3	m/s
Vent Depth	0.025 - 0.076	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break	113	MPa	ASTM D638
Tensile Strain, break	2.2	%	ASTM D638
Tensile Modulus, 50 mm/min	7580	MPa	ASTM D638
Flexural Stress	179	MPa	ASTM D790
Flexural Modulus	7510	MPa	ASTM D790
Tensile Stress, break	113	MPa	ISO 527
Tensile Strain, break	2.2	%	ISO 527
Tensile Modulus, 1 mm/min	7400	MPa	ISO 527
Flexural Stress	181	MPa	ISO 178
Flexural Modulus	7940	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.54	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.17	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.3	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.6	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	0.33	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.6	%	ISO 294
Density	1.54	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.23	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	203	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	204	°C	ISO 75/Af

Register for High value Multi-Point Data