FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 0.75 | mm | UL 94 |
LNP LUBRICOMP EFL36E compound is based on Polyetherimide (PEI) resin containing 30% glass fiber, 15% PTFE. Added features of this grade include: Easy Molding, Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 0.75 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 80 | J/m | ASTM D256 |
Izod Impact, unnotched, 23°C | 540 | J/m | ASTM D4812 |
Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
Izod Impact, unnotched 80*10*4 +23°C | 33 | kJ/m² | ISO 180/1U |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 14 | kJ/m² | ISO 179/1eA |
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 44 | kJ/m² | ISO 179/1eU |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 150 | °C | |
Drying Time | 4 - 6 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 360 - 375 | °C | |
Rear - Zone 1 Temperature | 355 - 365 | °C | |
Middle - Zone 2 Temperature | 360 - 370 | °C | |
Front - Zone 3 Temperature | 365 - 375 | °C | |
Nozzle Temperature | 365 - 375 | °C | |
Mold Temperature | 140 - 180 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw speed (Circumferential speed) | 0.2 - 0.3 | m/s | |
Vent Depth | 0.025 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Modulus, 5 mm/min | 11400 | MPa | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 2.3 | % | ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min | 140 | MPa | ASTM D638 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 8650 | MPa | ASTM D790 |
Flexural Strength, 1.3 mm/min, 50 mm span | 220 | MPa | ASTM D790 |
Tensile Strain, break, 5 mm/min | 2.4 | % | ISO 527 |
Tensile Stress, break, 5 mm/min | 150 | MPa | ISO 527 |
Tensile Modulus, 1 mm/min | 11200 | MPa | ISO 527 |
Flexural Modulus, 2 mm/min | 8900 | MPa | ISO 178 |
Flexural Strength, 2 mm/min | 210 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Dynamic COF | 0.77 | - | ASTM D3702 Modified: Manual |
Static COF | 0.63 | - | ASTM D3702 Modified: Manual |
Wear Factor Washer | 57 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
Moisture Absorption, (23°C/50% RH/24 hrs) | 0.1 - 0.2 | % | ASTM D570 |
Water Absorption, (23°C/24hrs) | 0.2 - 0.3 | % | ASTM D570 |
Density | 1.6 | g/cm³ | ASTM D792 |
Melt Flow Rate, 350°C/2.16 kgf | 8.2 | g/10 min | ASTM D1238 |
Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 |
Water Absorption, (23°C/24hrs) | 0.2 - 0.3 | % | ISO 62-1 |
Melt Volume Rate, MVR at 350°C/2.16kg | 5.3 | cm³/10 min | ISO 1133 |
Density | 1.6 | g/cm³ | ISO 1183 |
Mold Shrinkage, flow | 0.1 - 0.3 | % | SABIC method |
Mold Shrinkage, xflow | 0.2 - 0.5 | % | SABIC method |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 208 | °C | ASTM D648 |
Vicat Softening Temp, Rate B/50 | 215 | °C | ASTM D1525 |
CTE, 23°C to 60°C, flow | 1.6E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 4.1E-05 | 1/°C | ISO 11359-2 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 208 | °C | ISO 75/Af |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 213 | °C | ISO 75/Bf |
Vicat Softening Temp, Rate B/120 | 210 | °C | ISO 306 |
Vicat Softening Temp, Rate B/50 | 215 | °C | ISO 306 |
Relative Temp Index, Elec | 105 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 105 | °C | UL 746B |