IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 476 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 56 | J/m | ASTM D256 |
LNP LUBRICOMP EX10405H compound is based on Polyetherimide (PEI) resin containing 30% carbon and proprietary lubricant.. Added features of this grade include: Wear Resistant, Healthcare.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 476 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 56 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 150 | °C | |
Drying Time | 4 - 6 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 360 - 400 | °C | |
Rear - Zone 1 Temperature | 360 - 380 | °C | |
Middle - Zone 2 Temperature | 370 - 390 | °C | |
Front - Zone 3 Temperature | 380 - 400 | °C | |
Nozzle Temperature | 390 - 400 | °C | |
Mold Temperature | 140 - 180 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw speed (Circumferential speed) | 0.2 - 0.3 | m/s | |
Vent Depth | 0.025 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, brk, Type I, 5 mm/min | 216 | MPa | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 1.3 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 21540 | MPa | ASTM D638 |
Flexural Stress, brk, 1.3 mm/min, 50 mm span | 283 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 17300 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Wear Factor Washer | 22 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
Dynamic COF | 0.38 | - | ASTM D3702 Modified: Manual |
Static COF | 0.44 | - | ASTM D3702 Modified: Manual |
Specific Gravity | 1.4 | - | ASTM D792 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 213 | °C | ASTM D648 |