LNP™ LUBRICOMP™ Compound FL003

LNP LUBRICOMP FL003 compound is based on Polyethylene (PE) resin containing 15% PTFE. Added features of this grade include: Wear Resistant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyethylene, Unspecified (PE, Unspecified)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Wear resistant

Industry

Material previously used in

Building Component
Commercial Appliance
Electrical
Home Appliances
Mobile Phone - Computer - Tablets
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Lab Ware and Clinical Diagnostics
Medical Device

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	1460	J/m	ASTM D4812
Izod Impact, notched, 23°C	39	J/m	ASTM D256
Multiaxial Impact	4	J	ISO 6603
Instrumented Dart Impact Total Energy, 23°C	8	J	ASTM D3763
*Izod Impact, unnotched 80104 +23°C*	94	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	3	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	2 - 4	Hrs
Melt Temperature	230	°C
Front - Zone 3 Temperature	220 - 230	°C
Middle - Zone 2 Temperature	210 - 220	°C
Rear - Zone 1 Temperature	195 - 205	°C
Mold Temperature	40 - 55	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	24	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	14	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	8.5	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	59	%	ASTM D638
Tensile Modulus, 50 mm/min	1480	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	850	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	24	MPa	ISO 527
Tensile Stress, break, 5 mm/min	12	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	8.4	%	ISO 527
Tensile Strain, break, 5 mm/min	237	%	ISO 527
Tensile Modulus, 1 mm/min	1310	MPa	ISO 527
Flexural Stress	20	MPa	ISO 178
Flexural Modulus, 2 mm/min	920	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.03	-	ASTM D792
Density	1.03	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.04	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	1 - 3	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	1 - 3	%	ASTM D955
Moisture Absorption (23°C / 50% RH)	0.04	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	72	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	46	°C	ASTM D648
CTE, -30°C to 30°C, flow	1.34E-04	1/°C	ASTM D696
CTE, -30°C to 30°C, xflow	1.45E-04	1/°C	ASTM D696
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	82	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	46	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience