LNP LUBRICOMP FL003HL compound is based on Polyethylene (PE) resin containing 15% PTFE. Added features of this grade include Wear Resistant, Food Contact and Healthcare/Formula lock.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 1460 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 39 | J/m | ASTM D256 |
| Multiaxial Impact | 4 | J | ISO 6603 |
| Instrumented Dart Impact Total Energy, 23°C | 8 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 94 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 3 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 2 - 4 | Hrs | |
| Melt Temperature | 230 | °C | |
| Front - Zone 3 Temperature | 220 - 230 | °C | |
| Middle - Zone 2 Temperature | 210 - 220 | °C | |
| Rear - Zone 1 Temperature | 195 - 205 | °C | |
| Mold Temperature | 40 - 55 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 24 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 14 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 8.5 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 59 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 1480 | MPa | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 850 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 24 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 12 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 8.4 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 237 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1310 | MPa | ISO 527 |
| Flexural Stress | 20 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 920 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.03 | - | ASTM D792 |
| Density | 1.03 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.04 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 1 - 3 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 1 - 3 | % | ASTM D955 |
| Moisture Absorption (23°C / 50% RH) | 0.04 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 72 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 46 | °C | ASTM D648 |
| CTE, -30°C to 30°C, flow | 1.34E-04 | 1/°C | ASTM E831 |
| CTE, -30°C to 30°C, xflow | 1.45E-04 | 1/°C | ASTM E831 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 82 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 46 | °C | ISO 75/Af |