LNP LUBRICOMP GFL36L compound is based on Polysulfone (PSU) resin containing 30% glass fiber, 15% PTFE. Added features of this grade include: Low Extractable, Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | 23 | kJ/m² | ISO 180/1U |
| Multiaxial Impact | 3 | J | ISO 6603 |
| Izod Impact, notched, 23°C | 74 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | 341 | J/m | ASTM D4812 |
| Instrumented Dart Impact Energy @ peak, 23°C | 14 | J | ASTM D3763 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.05 | % | |
| Melt Temperature | 360 - 370 | °C | |
| Front - Zone 3 Temperature | 350 - 360 | °C | |
| Middle - Zone 2 Temperature | 340 - 350 | °C | |
| Rear - Zone 1 Temperature | 325 - 340 | °C | |
| Mold Temperature | 150 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield | 87 | MPa | ISO 527 |
| Tensile Stress, break | 87 | MPa | ISO 527 |
| Tensile Strain, yield | 1.3 | % | ISO 527 |
| Tensile Strain, break | 1.2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 9330 | MPa | ISO 527 |
| Flexural Stress | 121 | MPa | ISO 178 |
| Flexural Modulus | 9000 | MPa | ISO 178 |
| Tensile Stress, yield | 88 | MPa | ASTM D638 |
| Tensile Stress, break | 88 | MPa | ASTM D638 |
| Tensile Strain, yield | 1.3 | % | ASTM D638 |
| Tensile Strain, break | 1.3 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 10340 | MPa | ASTM D638 |
| Flexural Stress | 110 | MPa | ASTM D790 |
| Flexural Modulus | 8960 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.62 | g/cm³ | ISO 1183 |
| Mold Shrinkage, flow, 24 hrs | 0.26 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.51 | % | ISO 294 |
| Density | 1.62 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.1 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.2 - 0.4 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.4 - 0.6 | % | ASTM D955 |
| Wear Factor Washer | 44 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.42 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.62 | - | ASTM D3702 Modified: Manual |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 186 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 181 | °C | ISO 75/Af |
| CTE, -40°C to 40°C, flow | 2.40E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 3.0E-05 | 1/°C | ISO 11359-2 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 185 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 180 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 2.52E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 3.06E-05 | 1/°C | ASTM E831 |