LNP LUBRICOMP GL003XXP compound is based on Polysulfone (PSU) resin containing PTFE. Added features of this grade include: Internally Lubricated, Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 70 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.05 | % | |
| Melt Temperature | 360 - 370 | °C | |
| Front - Zone 3 Temperature | 350 - 360 | °C | |
| Middle - Zone 2 Temperature | 340 - 350 | °C | |
| Rear - Zone 1 Temperature | 325 - 340 | °C | |
| Mold Temperature | 150 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield, 5 mm/min | 60 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 6 - 7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1800 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 77 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2400 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage, flow | 0.5 - 0.8 | % | SABIC method |
| Density | 1.32 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 180 | °C | ISO 75/Af |