LNP LUBRICOMP GX07409H compound is based on Polysulfone (PSU) resin containing proprietary fillers. Added features of this grade include: Wear Resistant, Healthcare.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 219 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.05 | % | |
| Melt Temperature | 360 - 370 | °C | |
| Front - Zone 3 Temperature | 350 - 360 | °C | |
| Middle - Zone 2 Temperature | 340 - 350 | °C | |
| Rear - Zone 1 Temperature | 325 - 340 | °C | |
| Mold Temperature | 150 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield, 5 mm/min | 68 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 48 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 5.8 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 9.3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2520 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 88 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2640 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 0.51 - 0.71 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.63 - 0.83 | % | ASTM D955 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 167 | °C | ISO 75/Af |