LNP LUBRICOMP HFG25Z compound is based on Nylon 11 resin containing 25% glass fiber and graphite. Added features of this grade include: Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | 29 | kJ/m² | ISO 180/1U |
| Multiaxial Impact | 3 | J | ISO 6603 |
| Izod Impact, notched, 23°C | 69 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | 453 | J/m | ASTM D4812 |
| Instrumented Dart Impact Energy @ peak, 23°C | 15 | J | ASTM D3763 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 | % | |
| Melt Temperature | 225 - 260 | °C | |
| Front - Zone 3 Temperature | 260 - 270 | °C | |
| Middle - Zone 2 Temperature | 230 - 245 | °C | |
| Rear - Zone 1 Temperature | 200 - 210 | °C | |
| Mold Temperature | 45 - 55 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield, 5 mm/min | 76 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 76 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2.3 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 6830 | MPa | ISO 527 |
| Flexural Strength, 2 mm/min | 352 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 18200 | MPa | ISO 178 |
| Tensile Stress, yld, Type I, 5 mm/min | 153 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 153 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 2.8 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.8 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 11030 | MPa | ASTM D638 |
| Flexural Strength, 1.3 mm/min, 50 mm span | 98 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5520 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.3 | g/cm³ | ISO 1183 |
| Mold Shrinkage, flow, 24 hrs | 0.47 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.93 | % | ISO 294 |
| Density | 1.3 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.1 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.4 - 0.6 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.8 - 1 | % | ASTM D955 |
| Wear Factor Washer | 58 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.41 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.45 | - | ASTM D3702 Modified: Manual |
| Mold Shrinkage, flow | 0.47 | % | SABIC method |
| Mold Shrinkage, xflow | 0.93 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 182 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 166 | °C | ISO 75/Af |
| CTE, -40°C to 40°C, flow | 3.50E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 9.20E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, flow | 3.50E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 9.20E-05 | 1/°C | ISO 11359-2 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 182 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 171 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 3.42E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 9.18E-05 | 1/°C | ASTM E831 |