FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
LNP LUBRICOMP IBP34 compound is based on Nylon 6/12 resin containing 20% glass bead, 15% PTFE/silicone. Added features of this grade include: Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 329 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 28 | J/m | ASTM D256 |
Multiaxial Impact | 1 | J | ISO 6603 |
Instrumented Dart Impact Total Energy, 23°C | 4 | J | ASTM D3763 |
Izod Impact, unnotched 80*10*4 +23°C | 18 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 2 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.12 - 0.2 | % | |
Melt Temperature | 270 - 275 | °C | |
Front - Zone 3 Temperature | 270 - 280 | °C | |
Middle - Zone 2 Temperature | 260 - 270 | °C | |
Rear - Zone 1 Temperature | 255 - 265 | °C | |
Mold Temperature | 65 - 95 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, brk, Type I, 5 mm/min | 45 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 5 mm/min | 3.6 | % | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 3.9 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 2740 | MPa | ASTM D638 |
Flexural Stress, brk, 1.3 mm/min, 50 mm span | 76 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2610 | MPa | ASTM D790 |
Tensile Stress, break, 5 mm/min | 44 | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min | 3.5 | % | ISO 527 |
Tensile Strain, break, 5 mm/min | 3.7 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2670 | MPa | ISO 527 |
Flexural Stress | 73 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2650 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.32 | - | ASTM D792 |
Density | 1.32 | g/cm³ | ASTM D792 |
Moisture Absorption, (23°C/50% RH/24 hrs) | 0.22 | % | ASTM D570 |
Mold Shrinkage, flow, 24 hrs | 2 - 4 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 2 - 4 | % | ASTM D955 |
Wear Factor Washer | 13 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
Wear Factor Ring | 0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
Dynamic COF | 0.56 | - | ASTM D3702 Modified: Manual |
Static COF | 0.59 | - | ASTM D3702 Modified: Manual |
Moisture Absorption (23°C / 50% RH) | 0.26 | % | ISO 62 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 170 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 106 | °C | ASTM D648 |
CTE, -30°C to 30°C, flow | 8.8E-05 | 1/°C | ASTM D696 |
CTE, -30°C to 30°C, xflow | 8.7E-05 | 1/°C | ASTM D696 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 159 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 70 | °C | ISO 75/Af |
Relative Temp Index, Elec | 65 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 65 | °C | UL 746B |