LNP™ LUBRICOMP™ Compound IFL34

LNP LUBRICOMP IFL34 compound is based on Nylon 6/12 resin containing 20% glass fiber, 15% PTFE. Added features of this grade include: Wear Resistant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyamide 612 (Nylon 612)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Wear resistant

Industry

Material previously used in

Building Component
Commercial Appliance
Electrical
Home Appliances
Mobile Phone - Computer - Tablets
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Data Management

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	929	J/m	ASTM D4812
Izod Impact, notched, 23°C	96	J/m	ASTM D256
Instrumented Dart Impact Energy @ peak, 23°C	8	J	ASTM D3763
Multiaxial Impact	3	J	ISO 6603
*Izod Impact, unnotched 80104 +23°C*	53	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	9	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.12 - 0.2	%
Melt Temperature	270 - 275	°C
Front - Zone 3 Temperature	270 - 280	°C
Middle - Zone 2 Temperature	260 - 270	°C
Rear - Zone 1 Temperature	255 - 265	°C
Mold Temperature	65 - 95	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield	115	MPa	ASTM D638
Tensile Stress, break	115	MPa	ASTM D638
Tensile Strain, yield	3.1	%	ASTM D638
Tensile Strain, break	3.1	%	ASTM D638
Tensile Modulus, 50 mm/min	6890	MPa	ASTM D638
Flexural Stress	172	MPa	ASTM D790
Flexural Modulus	5510	MPa	ASTM D790
Tensile Stress, yield	121	MPa	ISO 527
Tensile Stress, break	121	MPa	ISO 527
Tensile Strain, yield	3	%	ISO 527
Tensile Strain, break	3	%	ISO 527
Tensile Modulus, 1 mm/min	7100	MPa	ISO 527
Flexural Stress	176	MPa	ISO 178
Flexural Modulus	6100	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.35	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.1	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.3 - 0.5	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	1 - 1.2	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	0.41	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1.1	%	ISO 294
Wear Factor Washer	18	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF	0.46	-	ASTM D3702 Modified: Manual
Static COF	0.47	-	ASTM D3702 Modified: Manual
Density	1.35	g/cm³	ISO 1183

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	212	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	197	°C	ASTM D648
CTE, -40°C to 40°C, flow	3.96E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	9.90E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	3.90E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	9.90E-05	1/°C	ISO 11359-2
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	212	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	195	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES