LNP LUBRICOMP IZL33 compound is based on Nylon 6/12 resin containing 15% milled glass and 15% PTFE. Added features of this grade include: Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 32 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | 188 | J/m | ASTM D4812 |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | 13 | kJ/m² | ISO 180/1U |
| Multiaxial Impact | 1.22 | J | ISO 6603 |
| Multiaxial Impact | 3.6 | J | ASTM D3763 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 82 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 271 - 276 | °C | |
| Front - Zone 3 Temperature | 271 - 282 | °C | |
| Middle - Zone 2 Temperature | 260 - 271 | °C | |
| Rear - Zone 1 Temperature | 254 - 265 | °C | |
| Mold Temperature | 65 - 93 | °C | |
| Back Pressure | 0.17 - 0.34 | MPa | |
| Screw Speed | 30 - 60 | rpm | |
| Maximum Moisture Content | 0.12 - 0.2 | % |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Flexural modulus | 2500 | MPa | ASTM D790 |
| Flexural Modulus | 2707 | MPa | ISO 178 |
| Flexural Stress | 73 | MPa | ASTM D790 |
| Tensile Modulus, 5 mm/min | 3410 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 4.6 | % | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3.3 | % | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 44 | MPa | ASTM D638 |
| Tensile Modulus, 1 mm/min | 3338 | MPa | ISO 527 |
| Tensile Stress, yield, 5 mm/min | 45 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 44 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 7 | % | ISO 527 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage, flow, 24 hrs | 1.9 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 1.7 | % | ASTM D955 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.15 | % | ASTM D570 |
| Moisture Absorption (23°C / 50% RH) | 0.11 | % | ISO 62 |
| Wear Factor Washer | 77 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.36 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.41 | - | ASTM D3702 Modified: Manual |
| Wear Factor Ring | 16.7 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Specific Gravity | 1.3 | - | ASTM D792 |
| Density | 1.29 | g/cm³ | ASTM D792 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.8 MPa, 3.2mm, unannealed | 128 | °C | ASTM D648 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 190 | °C | ASTM D648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 89 | °C | ISO 75/Af |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 175 | °C | ISO 75/Bf |
| CTE, -30°C to 30°C, flow | 0.000076 | 1/°C | ASTM E831 |
| CTE, -30°C to 30°C, xflow | 0.000088 | 1/°C | ASTM E831 |