LNP™ LUBRICOMP™ Compound JD4901

LNP LUBRICOMP JD4901 compound is based on Polyetherimide (PEI) resin containing 20% glass fiber, 10% PTFE. Added features of this grade include: Wear Resistant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyetherimide (PEI)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

High temperature resistance
Wear resistant

Industry

Material previously used in

Building Component
Commercial Appliance
Electrical
Home Appliances
Mobile Phone - Computer - Tablets
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Additive Semiconductor Materials
Amusement Machine
Circuit Protection
Electronic Components
Enclosure/Housing/Cover
Personal Computing
Semiconductor
electronic component
burn-in test socket
bits
test socket

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.6E+17	Ω/sq	ASTM D257
Volume Resistivity	5.8E+16	Ω.cm	ASTM D257
Dielectric Strength, in oil, 1.6 mm	23.6	kV/mm	ASTM D149
Dielectric Strength, in oil, 3.2 mm	16.7	kV/mm	ASTM D149

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	0.75	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	78	J/m	ASTM D256

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	150	°C
Drying Time	4 - 6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	380 - 410	°C
Nozzle Temperature	380 - 405	°C
Front - Zone 3 Temperature	380 - 410	°C
Middle - Zone 2 Temperature	370 - 400	°C
Rear - Zone 1 Temperature	360 - 390	°C
Mold Temperature	140 - 170	°C
Back pressure (Plastic Pressure)	5 - 10	MPa
Screw speed (Circumferential speed)	0.1 - 0.2	m/s
Shot to Cylinder Size	40 - 70	%

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield	125	MPa	SABIC - Japan Method
Tensile Strain, break	3	%	SABIC - Japan Method
Flexural Stress	190	MPa	ASTM D790
Flexural Modulus	6470	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.48	-	ASTM D792
Water Absorption, (23°C/24hrs)	0.18	%	ASTM D570
Water Absorption, (23°C/24hrs)	0.19	%	ISO 62-1
Water Absorption, (23°C/saturated)	1.01	%	ISO 62-1
Moisture Absorption, (23°C/50% RH/24hrs)	0.08	%	ISO 62-4
Mold Shrinkage, flow, 3.2 mm	0.2 - 0.3	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	213	°C	ASTM D648
Relative Temp Index, Elec	105	°C	UL 746B
Relative Temp Index, Mech w/impact	105	°C	UL 746B
Relative Temp Index, Mech w/o impact	105	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES