LNP LUBRICOMP JX91198 compound is based on Polyethersulfone (PES) resin containing 10% Carbon Fiber, 10% PTFE and proprietary lubricant. Added features of this grade include: Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 331 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 42 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy @ peak, 23°C | 4 | J | ASTM D3763 |
| Multiaxial Impact | 2 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 26 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.05 | % | |
| Melt Temperature | 355 - 370 | °C | |
| Front - Zone 3 Temperature | 370 - 380 | °C | |
| Middle - Zone 2 Temperature | 360 - 370 | °C | |
| Rear - Zone 1 Temperature | 345 - 355 | °C | |
| Mold Temperature | 140 - 150 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 116 | MPa | ASTM D638 |
| Tensile Strain, break | 1.9 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 10130 | MPa | ASTM D638 |
| Flexural Stress | 169 | MPa | ASTM D790 |
| Flexural Modulus | 8820 | MPa | ASTM D790 |
| Tensile Stress, break | 112 | MPa | ISO 527 |
| Tensile Strain, break | 1.8 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 9200 | MPa | ISO 527 |
| Flexural Stress | 161 | MPa | ISO 178 |
| Flexural Modulus | 9230 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.5 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.41 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.2 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.4 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 0.17 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.41 | % | ISO 294 |
| Wear Factor Washer | 4 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.43 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.34 | - | ASTM D3702 Modified: Manual |
| Density | 1.5 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.53 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 211 | °C | ASTM D648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 228 | °C | ISO 75/Af |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+02 - 1.E+05 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.05 | % | |
| Melt Temperature | 355 - 370 | °C | |
| Front - Zone 3 Temperature | 370 - 380 | °C | |
| Middle - Zone 2 Temperature | 360 - 370 | °C | |
| Rear - Zone 1 Temperature | 345 - 355 | °C | |
| Mold Temperature | 140 - 150 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 5 mm/min | 99 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.6 | % | ISO 527 |
| Flexural Stress, break, 2 mm/min | 140 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 6300 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage on Tensile Bar, flow | 0.3 - 0.5 | % | SABIC method |
| Wear Factor Washer | 20 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.34 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.27 | - | ASTM D3702 Modified: Manual |
| Density | 1.5 | g/cm³ | ISO 1183 |