LNP™ LUBRICOMP™ Compound KA000M

LNP LUBRICOMP KA000M compound is based on POM (Acetal) resin containing aramid powder and proprietary lubricant. Added features of this grade include: Internally Lubricated, Wear Resistant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Acetal (POM) Copolymer

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

No PFAS intentionally added
Wear resistant

Industry

Material previously used in

Building Component
Commercial Appliance
Electrical
Home Appliances
Mobile Phone - Computer - Tablets
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Prototype
ATM/Ticket Machine
Gear/Bearing/Slider
Wireless Communications
Irrigation

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94HB Flame Class Rating	≥1.5	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	28	J/m	ASTM D256
Izod Impact, unnotched, 23°C	310	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	3	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	25	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	2	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	30	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Melt Temperature	200 - 215	°C
Rear - Zone 1 Temperature	175 - 190	°C
Middle - Zone 2 Temperature	195 - 205	°C
Front - Zone 3 Temperature	210 - 220	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 5 mm/min	2600	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	5.3	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	6	%	ASTM D638
Tensile Stress, yld, Type I, 5 mm/min	42	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	2600	MPa	ASTM D790
Flexural Strength, 1.3 mm/min, 50 mm span	74	MPa	ASTM D790
Flexural Modulus, 2 mm/min	2400	MPa	ISO 178
Flexural Modulus, 2 mm/min, 60°C	1400	MPa	ISO 178
Flexural Modulus, 2 mm/min, 100°C	800	MPa	ISO 178
Flexural Strain, break, 2 mm/min	7	%	ISO 178
Flexural Strain, break, 2 mm/min, 60°C	7	%	ISO 178
Flexural Strain, break, 2 mm/min, 100°C	7	%	ISO 178
Flexural Stress, yield, 2 mm/min	70	MPa	ISO 178
Flexural Stress, yield, 2 mm/min, 60°C	42	MPa	ISO 178
Flexural Stress, yield, 2 mm/min, 100°C	22	MPa	ISO 178
Tensile Modulus, 1 mm/min	2600	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	6	%	ISO 527
Tensile Strain, break, 5 mm/min	7.8	%	ISO 527
Tensile Stress, yield, 5 mm/min	42	MPa	ISO 527

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Moisture Absorption, (23°C/50% RH/24 hrs)	0.2 - 0.3	%	ASTM D570
Water Absorption, (23°C/24hrs)	0.2 - 0.4	%	ASTM D570
Dynamic COF	0.2	-	ASTM D3702 Modified: Manual
Static COF	0.22	-	ASTM D3702 Modified: Manual
Wear Factor Washer	9	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Moisture Absorption (23°C / 50% RH)	0.2 - 0.3	%	ISO 62
Water Absorption, (23°C/24hrs)	0.2 - 0.4	%	ISO 62-1
Melt Volume Rate, MVR at 190°C/2.16 kg	4 - 6	cm³/10 min	ISO 1133
Density	1.35	g/cm³	ISO 1183
Mold Shrinkage, flow	1.5 - 2.5	%	SABIC method
Mold Shrinkage, xflow	1.5 - 2.5	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	96	°C	ASTM D648
Vicat Softening Temp, Rate B/50	143	°C	ASTM D1525
CTE, 23°C to 60°C, flow	1.2E-04	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	1.3E-04	1/°C	ISO 11359-2
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	90	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	150	°C	ISO 75/Bf
Vicat Softening Temp, Rate B/120	144	°C	ISO 306
Vicat Softening Temp, Rate B/50	143	°C	ISO 306

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas