LNP™ LUBRICOMP™ Compound KAL22

LNP LUBRICOMP KAL22 compound is based on Acetal (POM) Copolymer resin containing 10% PTFE, 10% aramid fiber. Added features of this grade include: Wear Resistant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Acetal (POM) Copolymer

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Wear resistant

Industry

Material previously used in

Building Component
Commercial Appliance
Electrical
Home Appliances
Mobile Phone - Computer - Tablets
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

ATM/Ticket Machine
Gear/Bearing/Slider
Industrial Material Handling
Irrigation

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Yellow Card Link 2	View	-	-
UL Recognized, 94HB Flame Class Rating	≥0.8	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	45	J/m	ASTM D256
Izod Impact, unnotched, 23°C	540	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	9	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	40	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	14	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	53	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Melt Temperature	200 - 215	°C
Rear - Zone 1 Temperature	175 - 190	°C
Middle - Zone 2 Temperature	195 - 205	°C
Front - Zone 3 Temperature	210 - 220	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 5 mm/min	3500	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	7.4	%	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	6.5	%	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	58	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	3400	MPa	ASTM D790
Flexural Strength, 1.3 mm/min, 50 mm span	83	MPa	ASTM D790
Tensile Modulus, 1 mm/min	3400	MPa	ISO 527
Tensile Strain, break, 5 mm/min	6.5	%	ISO 527
Tensile Strain, yield, 5 mm/min	5.9	%	ISO 527
Tensile Stress, yield, 5 mm/min	62	MPa	ISO 527
Flexural Modulus, 2 mm/min	3300	MPa	ISO 178
Flexural Strength, 2 mm/min	88	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.46	-	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.1	%	ASTM D570
Water Absorption, (23°C/24hrs)	0.2 - 0.4	%	ASTM D570
Dynamic COF	0.19	-	ASTM D3702 Modified: Manual
Static COF	0.22	-	ASTM D3702 Modified: Manual
Wear Factor Washer	29	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Melt Flow Rate, 230°C/10 kgf	13	g/10 min	ASTM D1238
Density	1.46	g/cm³	ISO 1183
Water Absorption, (23°C/24hrs)	0.2 - 0.4	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)	0.1	%	ISO 62
Melt Volume Rate, MVR at 230°C/10.0 kg	11	cm³/10 min	ISO 1133
Mold Shrinkage, flow	1 - 3	%	SABIC method
Mold Shrinkage, xflow	1 - 3	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	162	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	120	°C	ASTM D648
CTE, 23°C to 60°C, flow	7.7E-05	1/°C	ASTM E831
CTE, 23°C to 60°C, xflow	1.2E-04	1/°C	ASTM E831
Vicat Softening Temp, Rate B/50	152	°C	ASTM D1525
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	104	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	152	°C	ISO 75/Bf
Vicat Softening Temp, Rate B/120	153	°C	ISO 306
Vicat Softening Temp, Rate B/50	152	°C	ISO 306
CTE, 23°C to 60°C, flow	7.7E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	1.2E-04	1/°C	ISO 11359-2

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES