LNP LUBRICOMP KFL32R compound is based on Acetal (POM) Copolymer resin containing 10% glass fiber, 15% PTFE. Added features of this grade include: Easy Release, Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 347 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 42 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy @ peak, 23°C | 6 | J | ASTM D3763 |
| Multiaxial Impact | 1 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 26 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 200 - 215 | °C | |
| Front - Zone 3 Temperature | 210 - 220 | °C | |
| Middle - Zone 2 Temperature | 195 - 205 | °C | |
| Rear - Zone 1 Temperature | 175 - 190 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 79 | MPa | ASTM D638 |
| Tensile Strain, break | 2.6 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 5100 | MPa | ASTM D638 |
| Flexural Stress | 115 | MPa | ASTM D790 |
| Flexural Modulus | 4820 | MPa | ASTM D790 |
| Tensile Stress, break | 79 | MPa | ISO 527 |
| Tensile Strain, break | 2.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 5400 | MPa | ISO 527 |
| Flexural Stress | 122 | MPa | ISO 178 |
| Flexural Modulus | 5800 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.56 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.18 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 1.1 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 1.3 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 1.08 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 1.34 | % | ISO 294 |
| Density | 1.56 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.33 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 165 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 161 | °C | ASTM D648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 162 | °C | ISO 75/Af |