LNP LUBRICOMP KFP032 compound is based on Acetal (POM) Copolymer resin containing 10% glass fiber, 25% PTFE/silicone. Added features of this grade include: Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 381 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 40 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 5 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 24 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 3 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 200 - 215 | °C | |
| Front - Zone 3 Temperature | 210 - 220 | °C | |
| Middle - Zone 2 Temperature | 195 - 205 | °C | |
| Rear - Zone 1 Temperature | 175 - 190 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 67 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.6 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 5020 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 100 | MPa | ASTM D790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 94 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 4180 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 64 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 4810 | MPa | ISO 527 |
| Flexural Stress | 95 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 4120 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.52 | - | ASTM D792 |
| Density | 1.51 | g/cm³ | ASTM D792 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 162 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 155 | °C | ASTM D648 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 161 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 148 | °C | ISO 75/Af |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 40 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 57 | MPa | ASTM D638 |
| Tensile Strain, break | 2.5 | % | ASTM D638 |
| Flexural Stress | 82 | MPa | ASTM D790 |
| Flexural Modulus | 3720 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.51 | g/cm³ | ASTM D792 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 155 | °C | ASTM D648 |