LNP LUBRICOMP KI001 compound is based on POM (Acetal) resin containing silicone. Added features of this grade include: Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 4.2 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | 57 | kJ/m² | ISO 180/1U |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Time | 2 - 3 | Hrs | |
| Drying Temperature | 80 | °C | |
| Front - Zone 3 Temperature | 200 - 220 | °C | |
| Middle - Zone 2 Temperature | 190 - 210 | °C | |
| Rear - Zone 1 Temperature | 180 - 200 | °C | |
| Mold Temperature | 80 - 100 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Modulus, 1 mm/min | 2500 | MPa | ISO 527 |
| Tensile Stress, yield, 5 mm/min | 44 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 20 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/min | 2000 | MPa | ISO 178 |
| Flexural Stress, yield, 2 mm/min | 65 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage, flow | 2.5 | % | SABIC method |
| Wear Factor Washer | 66 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.2 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.3 | - | ASTM D3702 Modified: Manual |
| Density | 1.38 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, -30°C to 30°C, flow | 1.05E-04 | 1/°C | ISO 11359-2 |
| CTE, -30°C to 30°C, xflow | 1.23E-04 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 87 | °C | ISO 75/Af |