FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
LNP LUBRICOMP KL004A compound is based on Acetal (POM) Homopolymer resin containing 20% PTFE. Added features of this grade include: Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 560 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 42 | J/m | ASTM D256 |
Instrumented Dart Impact Energy @ peak, 23°C | 7 | J | ASTM D3763 |
Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 | Hrs | |
Melt Temperature | 200 - 215 | °C | |
Front - Zone 3 Temperature | 210 - 220 | °C | |
Middle - Zone 2 Temperature | 195 - 205 | °C | |
Rear - Zone 1 Temperature | 175 - 190 | °C | |
Mold Temperature | 80 - 110 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 56 | MPa | ASTM D638 |
Tensile Strain, break | 11.4 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 2550 | MPa | ASTM D638 |
Flexural Stress | 86 | MPa | ASTM D790 |
Flexural Modulus | 2620 | MPa | ASTM D790 |
Tensile Stress, break | 50 | MPa | ISO 527 |
Tensile Strain, break | 9.4 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2400 | MPa | ISO 527 |
Flexural Stress | 86 | MPa | ISO 178 |
Flexural Modulus | 2900 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.52 | g/cm³ | ASTM D792 |
Moisture Absorption, (23°C/50% RH/24 hrs) | 0.23 | % | ASTM D570 |
Mold Shrinkage, flow, 24 hrs | 2 - 2.2 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 2 - 2.2 | % | ASTM D955 |
Mold Shrinkage, flow, 24 hrs | 2 - 2.19 | % | ISO 294 |
Mold Shrinkage, xflow, 24 hrs | 2 - 2.19 | % | ISO 294 |
Wear Factor Washer | 12 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
Dynamic COF | 0.23 | - | ASTM D3702 Modified: Manual |
Static COF | 0.09 | - | ASTM D3702 Modified: Manual |
Density | 1.52 | g/cm³ | ISO 1183 |
Moisture Absorption (23°C / 50% RH) | 0.4 | % | ISO 62 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 95 | °C | ASTM D648 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 98 | °C | ISO 75/Af |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 560 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 42 | J/m | ASTM D256 |
Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, brk, Type I, 5 mm/min | 56 | MPa | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 11.4 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 2550 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 86 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2620 | MPa | ASTM D790 |
Tensile Strain, break, 5 mm/min | 9.4 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2400 | MPa | ISO 527 |
Flexural Modulus, 2 mm/min | 2400 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Moisture Absorption, (23°C/50% RH/24 hrs) | 0.23 | % | ASTM D570 |
Mold Shrinkage, flow, 24 hrs | 2 - 2.2 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 2 - 2.2 | % | ASTM D955 |
Wear Factor Washer | 12 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
Dynamic COF | 0.23 | - | ASTM D3702 Modified: Manual |
Static COF | 0.09 | - | ASTM D3702 Modified: Manual |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 95 | °C | ASTM D648 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 98 | °C | ISO 75/Af |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 | Hrs | |
Melt Temperature | 200 - 215 | °C | |
Front - Zone 3 Temperature | 210 - 220 | °C | |
Middle - Zone 2 Temperature | 195 - 205 | °C | |
Rear - Zone 1 Temperature | 175 - 190 | °C | |
Mold Temperature | 80 - 110 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield, 5 mm/min | 46 | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min | 10 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2400 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 74 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2400 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Mold Shrinkage, flow, 24 hrs | 2 - 2.2 | % | ASTM D955 |
Wear Factor Washer | 12 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
Dynamic COF | 0.23 | - | ASTM D3702 Modified: Manual |
Static COF | 0.09 | - | ASTM D3702 Modified: Manual |
Density | 1.52 | g/cm³ | ISO 1183 |
Moisture Absorption (23°C / 50% RH) | 0.4 | % | ISO 62 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 157 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 98 | °C | ISO 75/Af |