LNP LUBRICOMP LCL33 compound is based on Polyetheretherketone (PEEK) resin containing 15% carbon fiber, 15% PTFE. Added features of this grade include: Wear Resistant, Electrically Conductive.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 480 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 64 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy @ peak, 23°C | 9 | J | ASTM D3763 |
| Multiaxial Impact | 9 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 34 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Front - Zone 3 Temperature | 380 - 400 | °C | |
| Middle - Zone 2 Temperature | 380 - 400 | °C | |
| Rear - Zone 1 Temperature | 370 - 380 | °C | |
| Mold Temperature | 175 - 190 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 179 | MPa | ASTM D638 |
| Tensile Strain, break | 1.7 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 16610 | MPa | ASTM D638 |
| Flexural Stress | 262 | MPa | ASTM D790 |
| Flexural Modulus | 12960 | MPa | ASTM D790 |
| Tensile Stress, break | 187 | MPa | ISO 527 |
| Tensile Strain, break | 1.6 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 14500 | MPa | ISO 527 |
| Flexural Stress | 230 | MPa | ISO 178 |
| Flexural Modulus | 11700 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.07 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.1 - 0.3 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.4 - 0.7 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 0.1 - 0.3 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.3 - 0.7 | % | ISO 294 |
| Wear Factor Washer | 17 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.35 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.28 | - | ASTM D3702 Modified: Manual |
| Density | 1.43 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | >298 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 2.34E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 4.14E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 2.36E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 4.17E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | >300 | °C | ISO 75/Af |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+03 - 1.E+05 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 34 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.1 | % | |
| Melt Temperature | 380 - 390 | °C | |
| Front - Zone 3 Temperature | 380 - 395 | °C | |
| Middle - Zone 2 Temperature | 365 - 375 | °C | |
| Rear - Zone 1 Temperature | 350 - 360 | °C | |
| Mold Temperature | 140 - 165 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 5 mm/min | 162 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 14500 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 230 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 2.7 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 11700 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min, 80°C | 2.7 | % | ISO 178 |
| Flexural Strain, break, 2 mm/min, 120°C | 2.7 | % | ISO 178 |
| Flexural Strain, break, 2 mm/min, 150°C | 6 | % | ISO 178 |
| Flexural Strain, break, 2 mm/min, 200°C | 6.3 | % | ISO 178 |
| Flexural Strain, break, 2 mm/min, 250°C | 6.5 | % | ISO 178 |
| Flexural Stress, yield, 2 mm/min, 80°C | 192 | MPa | ISO 178 |
| Flexural Stress, yield, 2 mm/min, 120°C | 158 | MPa | ISO 178 |
| Flexural Stress, yield, 2 mm/min, 150°C | 100 | MPa | ISO 178 |
| Flexural Stress, yield, 2 mm/min, 200°C | 60 | MPa | ISO 178 |
| Flexural Stress, yield, 2 mm/min, 250°C | 50 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min, 80°C | 10300 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min, 120°C | 10200 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min, 150°C | 5700 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min, 200°C | 3000 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Wear Factor Washer | 17 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.35 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.28 | - | ASTM D3702 Modified: Manual |
| Density | 1.43 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 400°C/10.0 kg | 6 - 8 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, 23°C to 60°C, flow | 9.5E-06 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 5.3E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | >300 | °C | ISO 75/Af |