LNP LUBRICOMP LCL36E compound is based on Polyetheretherketone (PEEK) resin containing 30% carbon fiber and 15% PTFE. Added features of this grade include: Easy Molding, Wear Resistant, Electrically Conductive.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 651 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 83 | J/m | ASTM D256 |
| Multiaxial Impact | 3 | J | ISO 6603 |
| Instrumented Dart Impact Total Energy, 23°C | 11 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Front - Zone 3 Temperature | 380 - 400 | °C | |
| Middle - Zone 2 Temperature | 380 - 400 | °C | |
| Rear - Zone 1 Temperature | 370 - 380 | °C | |
| Mold Temperature | 175 - 190 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 208 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.6 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 21440 | MPa | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 357 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 23000 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 140 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 17520 | MPa | ISO 527 |
| Flexural Stress | 321 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 22720 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.51 | - | ASTM D792 |
| Density | 1.5 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.04 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.31 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.81 | % | ASTM D955 |
| Wear Factor Washer | 18 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Wear Factor Ring | 1 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.38 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.38 | - | ASTM D3702 Modified: Manual |
| Moisture Absorption (23°C / 50% RH) | 0.04 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 342 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 332 | °C | ASTM D648 |
| CTE, -30°C to 30°C, flow | 1.4E-05 | 1/°C | ASTM D696 |
| CTE, -30°C to 30°C, xflow | 2.9E-05 | 1/°C | ASTM D696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 342 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 329 | °C | ISO 75/Af |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+01 - 1.E+03 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.1 | % | |
| Melt Temperature | 380 - 390 | °C | |
| Front - Zone 3 Temperature | 380 - 395 | °C | |
| Middle - Zone 2 Temperature | 365 - 375 | °C | |
| Rear - Zone 1 Temperature | 350 - 360 | °C | |
| Mold Temperature | 140 - 165 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 5 mm/min | 224 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 21600 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 317 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 19800 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.5 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, 23°C to 60°C, flow | 8.4E-06 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 4.2E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | >300 | °C | ISO 75/Af |