LNP LUBRICOMP LL003XX1 compound is based on Polyetheretherketone (PEEK) resin containing 15% PTFE lubricant. Added features of this grade include: Easy Molding, Excellent Wear Resistance and Very Low Coefficient of Friction (CoF)
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Dielectric Constant, 1.1 GHz | 3 | - | SABIC method |
| Dielectric Constant, 1.9 GHz | 0.0026 | - | SABIC method |
| Dissipation Factor, 1.1 GHz | 3.01 | - | SABIC method |
| Dissipation Factor, 1.9 GHz | 0.0028 | - | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 76 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | 1230 | J/m | ASTM D4812 |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | 95 | kJ/m² | ISO 180/1U |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 135 | kJ/m² | ISO 179/1eU |
| Multiaxial Impact | 2.46 | J | ASTM D3763 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 3 - 5 | Hrs | |
| Nozzle Temperature | 380 - 400 | °C | |
| Melt Temperature | 380 - 400 | °C | |
| Front - Zone 3 Temperature | 370 - 380 | °C | |
| Middle - Zone 2 Temperature | 360 - 370 | °C | |
| Rear - Zone 1 Temperature | 290 - 300 | °C | |
| Mold Temperature | 170 - 200 | °C | |
| Screw Speed | 50 - 100 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Flexural Strength, 1.3 mm/min, 50 mm span | 121 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3100 | MPa | ASTM D790 |
| Tensile Stress, brk, Type I, 5 mm/min | 75 | MPa | ASTM D638 |
| Tensile Modulus, 5 mm/min | 3200 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 50 | % | ASTM D638 |
| Flexural Strength, 2 mm/min | 123 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2900 | MPa | ISO 178 |
| Tensile Stress, break, 5 mm/min | 70 | MPa | ISO 527 |
| Tensile Modulus, 1 mm/min | 3100 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 15 | % | ISO 527 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Dynamic COF | 0.29 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.25 | - | ASTM D3702 Modified: Manual |
| Wear Factor Ring | 36 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Specific Gravity | 1.36 | - | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 0.3 - 0.4 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.4 - 0.5 | % | ASTM D955 |
| Density | 1.36 | g/cm³ | ASTM D792 |
| Moisture Absorption (23°C / 50% RH) | 0.01 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 148 | °C | ASTM D648 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 162 | °C | ASTM D648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 148 | °C | ISO 75/Af |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 172 | °C | ISO 75/Bf |
| CTE, -40°C to 120°C, flow | 4.9E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 120°C, xflow | 5.8E-05 | 1/°C | ASTM E831 |