LNP LUBRICOMP MX06404 compound is based on Polypropylene (PP) resin containing 20% glass fiber and 15% PTFE. Added features of this grade include: Heat Stabilized, Low Extractable, Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 150 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 40 | J/m | ASTM D256 |
| Multiaxial Impact | 2 | J | ISO 6603 |
| Instrumented Dart Impact Total Energy, 23°C | 11 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 3 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 225 - 250 | °C | |
| Front - Zone 3 Temperature | 240 - 250 | °C | |
| Middle - Zone 2 Temperature | 215 - 225 | °C | |
| Rear - Zone 1 Temperature | 195 - 205 | °C | |
| Mold Temperature | 30 - 50 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 39 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 33 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 1.2 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.6 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 5730 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 61 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 4480 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 38 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 36 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 1.1 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 5320 | MPa | ISO 527 |
| Flexural Stress | 59 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 4580 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.13 | - | ASTM D792 |
| Density | 1.14 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.13 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.7 - 0.9 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 1 - 3 | % | ASTM D955 |
| Wear Factor Washer | 61 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Wear Factor Ring | 1 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.3 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.28 | - | ASTM D3702 Modified: Manual |
| Moisture Absorption (23°C / 50% RH) | 0.07 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 145 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 103 | °C | ASTM D648 |
| CTE, -30°C to 30°C, flow | 6.1E-05 | 1/°C | ASTM D696 |
| CTE, -30°C to 30°C, xflow | 8.4E-05 | 1/°C | ASTM D696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 135 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 97 | °C | ISO 75/Af |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 150 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 40 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 35 | MPa | ASTM D638 |
| Tensile Strain, break | 1 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 5810 | MPa | ASTM D638 |
| Flexural Stress | 55 | MPa | ASTM D790 |
| Flexural Modulus | 4820 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ASTM D792 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 103 | °C | ASTM D648 |