LNP™ LUBRICOMP™ Compound NX20BSR

LNP LUBRICOMP NX20BSR compound is based on a low-gloss black Polycarbonate / Acrylonitrile Butadiene Styrene (PC/ABS) blend with good Buzz, Squeak and Rattle (BSR) performance. Added features of this grade include: Low Slip-Stick, Internally Lubricated and Wear Resistant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate + ABS (PC+ABS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

No PFAS intentionally added
Wear resistant

Industry

Material previously used in

Automotive Interiors
Building Component
Commercial Appliance
Electrical
Home Appliances
Mobile Phone - Computer - Tablets
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Automotive
Console
Infotainment/Telematic
Interior
Interior trims
bsr
buzz
squeak
rattle
automotive interior
car navigation
door trim
back mirror

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, unnotched 80104 +23°C*	208	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	40	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 -30°C*	248	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 -40°C*	14	kJ/m²	ISO 180/1A
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	402	kJ/m²	ISO 179/1eU
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	49	kJ/m²	ISO 179/1eA
*Charpy -40°C, V-notch Edgew 80104 sp=62mm*	16	kJ/m²	ISO 179/1eA
Izod Impact, notched, 23°C	747	J/m	ASTM D256
Izod Impact, notched, -30°C	463	J/m	ASTM D256

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	105 - 110	°C
Drying Time (Cumulative)	3 - 4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	275 - 300	°C
Front - Zone 3 Temperature	260 - 300	°C
Middle - Zone 2 Temperature	255 - 295	°C
Rear - Zone 1 Temperature	250 - 290	°C
Mold Temperature	60 - 80	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 1 mm/min	2170	MPa	ISO 527
Tensile Stress, yield, 50 mm/min	50	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5	%	ISO 527
Tensile Stress, break, 50 mm/min	44	MPa	ISO 527
Tensile Strain, break, 50 mm/min	67	%	ISO 527
Flexural Modulus, 2 mm/min	2090	MPa	ISO 178
Tensile Modulus, 50 mm/min	2280	MPa	ASTM D638
Tensile Stress, yld, Type I, 50 mm/min	56	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	5	%	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	46	MPa	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	86	%	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	2180	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.12	g/cm³	ISO 1183
Dynamic COF	0.33	-	ASTM D3702 Modified: Manual
Moisture Absorption, (23°C/50% RH/24 hrs)	0.097	%	ASTM D570
Mold Shrinkage, flow	0.7 - 0.9	%	SABIC method
Mold Shrinkage, xflow	0.8 - 1	%	SABIC method
Melt Volume Rate, MVR at 260°C/5.0 kg	21	cm³/10 min	ISO 1133
Melt Flow Rate, 260°C/5.0 kgf	23	g/10 min	ASTM D1238

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	104	°C	ISO 75/Af
Vicat Softening Temp, Rate B/50	126	°C	ISO 306
Vicat Softening Temp, Rate B/120	124	°C	ISO 306
HDT, 0.45 MPa, 3.2 mm, unannealed	125	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	103	°C	ASTM D648

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES