LNP™ LUBRICOMP™ Compound OCL36A

LNP LUBRICOMP OCL36A compound is based on Polyphenylene Sulfide (PPS) - branched resin containing 30% carbon fiber, 15% PTFE. Added features of this grade include: Electrically Conductive, Wear Resistant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyphenylene Sulfide, Branched (PPS, Branched)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Carbon fiber filled
Electrically Conductive
High stiffness/Strength
Wear resistant

Industry

Material previously used in

Building Component
Commercial Appliance
Electrical
Home Appliances
Mobile Phone - Computer - Tablets
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Data Management
Document Handling
Oil/Gas

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	48	J/m	ASTM D256

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120 - 150	°C
Drying Time	4	Hrs
Melt Temperature	315 - 340	°C
Front - Zone 3 Temperature	330 - 345	°C
Middle - Zone 2 Temperature	320 - 330	°C
Rear - Zone 1 Temperature	305 - 315	°C
Mold Temperature	140 - 165	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break	158	MPa	ASTM D638
Tensile Strain, break	1 - 3	%	ASTM D638
Flexural Modulus	23160	MPa	ASTM D790

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	264	°C	ASTM D648

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	48	J/m	ASTM D256

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120 - 150	°C
Drying Time	4	Hrs
Melt Temperature	315 - 340	°C
Front - Zone 3 Temperature	330 - 345	°C
Middle - Zone 2 Temperature	320 - 330	°C
Rear - Zone 1 Temperature	305 - 315	°C
Mold Temperature	140 - 165	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break	158	MPa	ASTM D638
Tensile Strain, break	1 - 3	%	ASTM D638
Flexural Modulus	23160	MPa	ASTM D790

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	264	°C	ASTM D648

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+01 - 1.E+03	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80103 -40°C*	6	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	26	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -40°C*	23	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	6	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120 - 150	°C
Drying Time	4	Hrs
Melt Temperature	315 - 340	°C
Front - Zone 3 Temperature	330 - 345	°C
Middle - Zone 2 Temperature	320 - 330	°C
Rear - Zone 1 Temperature	305 - 315	°C
Mold Temperature	140 - 165	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break, 5 mm/min	153	MPa	ISO 527
Tensile Strain, break, 5 mm/min	0.7	%	ISO 527
Tensile Modulus, 1 mm/min	25000	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	261	MPa	ISO 178
Flexural Stress, break, 2 mm/min	217	MPa	ISO 178
Flexural Strain, break, 2 mm/min	1.3	%	ISO 178
Flexural Modulus, 2 mm/min	21200	MPa	ISO 178
Flexural Strain, break, 2 mm/min, 80°C	1.3	%	ISO 178
Flexural Strain, break, 2 mm/min, 120°C	2.3	%	ISO 178
Flexural Strain, break, 2 mm/min, 150°C	2.4	%	ISO 178
Flexural Strain, break, 2 mm/min, 200°C	2.4	%	ISO 178
Flexural Stress, yield, 2 mm/min, 80°C	212	MPa	ISO 178
Flexural Stress, yield, 2 mm/min, 120°C	118	MPa	ISO 178
Flexural Stress, yield, 2 mm/min, 150°C	94	MPa	ISO 178
Flexural Stress, yield, 2 mm/min, 200°C	66	MPa	ISO 178
Flexural Modulus, 2 mm/min, 80°C	20600	MPa	ISO 178
Flexural Modulus, 2 mm/min, 120°C	10200	MPa	ISO 178
Flexural Modulus, 2 mm/min, 150°C	7900	MPa	ISO 178
Flexural Modulus, 2 mm/min, 200°C	6100	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Mold Shrinkage, flow, 24 hrs	0.19	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.95	%	ISO 294
Wear Factor Washer	19	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF	0.39	-	ASTM D3702 Modified: Manual
Density	1.52	g/cm³	ISO 1183
Water Absorption, (23°C/24hrs)	0.05	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)	0.03	%	ISO 62
Melt Volume Rate, MVR at 315°C/5.0 kg	4 - 6	cm³/10 min	ISO 1133

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Heat	1633	J/kg-K	ASTM E1269
CTE, 23°C to 60°C, flow	3.E-06	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	4.9E-05	1/°C	ISO 11359-2
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	278	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	255	°C	ISO 75/Af
Thermal Conductivity	0.36	W/m-K	ASTM D5930

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES

LNP™ LUBRICOMP™ Compound OCL36A

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

IMPACT

INJECTION MOLDING

MECHANICAL

THERMAL

IMPACT

INJECTION MOLDING

MECHANICAL

THERMAL

ELECTRICAL

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL