ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Comparative Tracking Index | 175 | V | IEC 60112 |
LNP LUBRICOMP OFL38A compound is based on Polyphenylene Sulfide (PPS) branched resin containing 40% glass fiber and 15% PTFE. Added features of this grade include: Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Comparative Tracking Index | 175 | V | IEC 60112 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 1.7 | mm | UL 94 |
Glow Wire Ignitability Temperature, 2.0 mm | 875 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature, 1.0 mm | 825 | °C | IEC 60695-2-13 |
Glow Wire Flammability Index, 2.0 mm | 960 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index, 1.0 mm | 960 | °C | IEC 60695-2-12 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 - 150 | °C | |
Drying Time | 4 | Hrs | |
Melt Temperature | 315 - 320 | °C | |
Front - Zone 3 Temperature | 330 - 345 | °C | |
Middle - Zone 2 Temperature | 320 - 330 | °C | |
Rear - Zone 1 Temperature | 305 - 315 | °C | |
Mold Temperature | 140 - 165 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break, 5 mm/min | 147 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 14700 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 206 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 12700 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Mold Shrinkage, flow | 0.2 | % | SABIC method |
Density | 1.8 | g/cm³ | ISO 1183 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
CTE, 23°C to 60°C, flow | 1.6E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 3.8E-05 | 1/°C | ISO 11359-2 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 280 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 264 | °C | ISO 75/Af |
Relative Temp Index, Elec | 130 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 130 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 130 | °C | UL 746B |