LNP™ LUBRICOMP™ Compound OL003A

LNP LUBRICOMP OL003A compound is based on Polyphenylene Sulfide (PPS) - branched resin containing 15% PTFE. Added features of this grade include: Wear Resistant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyphenylene Sulfide, Branched (PPS, Branched)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Wear resistant

Industry

Material previously used in

Building Component
Commercial Appliance
Electrical
Home Appliances
Mobile Phone - Computer - Tablets
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Document Handling

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	74	J/m	ASTM D4812
Izod Impact, notched, 23°C	13	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	1	J	ASTM D3763
*Izod Impact, unnotched 80104 +23°C*	4	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	2	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120 - 150	°C
Drying Time	4	Hrs
Melt Temperature	315 - 320	°C
Front - Zone 3 Temperature	330 - 345	°C
Middle - Zone 2 Temperature	320 - 330	°C
Rear - Zone 1 Temperature	305 - 315	°C
Mold Temperature	140 - 165	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	21	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	0.6	%	ASTM D638
Tensile Modulus, 5 mm/min	3590	MPa	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	65	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	3870	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	20	MPa	ISO 527
Tensile Strain, break, 5 mm/min	0.6	%	ISO 527
Tensile Modulus, 1 mm/min	3360	MPa	ISO 527
Flexural Strength, 2 mm/min	56	MPa	ISO 178
Flexural Modulus, 2 mm/min	3320	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.44	-	ASTM D792
Density	1.43	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.02	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.9 - 2	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	1 - 3	%	ASTM D955
Moisture Absorption (23°C / 50% RH)	0.04	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	175	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	108	°C	ASTM D648
CTE, -30°C to 30°C, flow	6.E-05	1/°C	ASTM D696
CTE, -30°C to 30°C, xflow	6.6E-05	1/°C	ASTM D696
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	178	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	109	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES